- Acrylonitrile Butadiene Styrene (ABS), 10% Glass Fiber Filled
- Ineos ABS Lustran® ABS 150G10 10% Glass Fiber Reinforced Grade
Ineos ABS Lustran® ABS 150G10 10% Glass Fiber Reinforced Grade
| Category | Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS), 10% Glass Fiber Filled |
| Manufacturer | Ineos ABS |
| Trade Name | Lustran® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Ineos ABS Lustran® ABS 150G10 10% Glass Fiber Reinforced Grade.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.13 g/cc | 0.0408 lb/in³ | ISO 1183 |
| Linear Mold Shrinkage, Transverse | 0.0020 - 0.0040 cm/cm | 0.0020 - 0.0040 in/in | Test Condition: 60x60x2; ISO 294-4 |
| Melt Flow | 19 g/10 min @Load 10.0 kg, Temperature 220 °C |
19 g/10 min @Load 22.0 lb, Temperature 428 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 74.0 MPa | 10700 psi | 50 mm/min; ISO 527-1,-2 |
| Elongation at Break | 5.0 % | 5.0 % | 50 mm/min; acc. ISO 527-1,-2 |
| Tensile Modulus | 4.40 GPa | 638 ksi | 1 mm/min; ISO 527-1,-2 |
| Flexural Strength | 100 MPa | 14500 psi | 2 mm/min; ISO 178 |
| Flexural Modulus | 4.20 GPa | 609 ksi | 2 mm/min; ISO 178 |
| Izod Impact, Notched (ISO) | 16.0 kJ/m² | 7.61 ft-lb/in² | ISO 180-1A |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 110 °C | 230 °F | ISO 75-1,-2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 114 °C | 237 °F | ISO 75-1,-2 |
| Vicat Softening Point | 105 °C @Load 5.10 kg |
221 °F @Load 11.2 lb |
50°C/hour; ISO 306 |
| Flammability, UL94 | HB @Thickness 1.60 mm |
HB @Thickness 0.0630 in |