Ineos ABS Lustran® 256 Extrusion Blending Grade
| Category | Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS), Extruded |
| Manufacturer | Ineos ABS |
| Trade Name | Lustran® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Ineos ABS Lustran® 256 Extrusion Blending Grade.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Lustran® ABS 256 resin is a natural, medium-flow, medium-impact, low-gloss, low-gel extrusion grade of ABS (Acrylonitrile Butadiene Styrene). It is used for blending with other Lustran® ABS virgin and regrind materials to optimize cost and performance.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.05 g/cc | 0.0379 lb/in³ | ASTM-D792 |
| Melt Flow | 14 g/10 min @Load 10.0 kg, Temperature 230 °C |
14 g/10 min @Load 22.0 lb, Temperature 446 °F |
ASTM-D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 40.0 MPa | 5800 psi | ASTM-D638 |
| Tensile Modulus | 2.20 GPa | 319 ksi | ASTM-D638 |
| Flexural Yield Strength | 69.0 MPa | 10000 psi | ASTM-D790 |
| Flexural Modulus | 2.40 GPa | 348 ksi | ASTM-D790 |
| Izod Impact, Notched | 0.480 J/cm @Thickness 3.20 mm, Temperature -40.0 °C |
0.899 ft-lb/in @Thickness 0.126 in, Temperature -40.0 °F |
ASTM-D256 |
| 0.850 J/cm @Thickness 3.20 mm, Temperature -18.0 °C |
1.59 ft-lb/in @Thickness 0.126 in, Temperature -0.400 °F |
ASTM-D256 | |
| 1.60 J/cm @Thickness 3.20 mm, Temperature 23.0 °C |
3.00 ft-lb/in @Thickness 0.126 in, Temperature 73.4 °F |
ASTM-D256 | |
| Impact Test | 12.0 J @Temperature -40.0 °C |
8.85 ft-lb @Temperature -40.0 °F |
Instrumented Impact (0.5-in. dart, 3-in. clamp, 7.6 mph); Peak Energy; ASTM-D3763 |
| 14.0 J @Temperature -40.0 °C |
10.3 ft-lb @Temperature -40.0 °F |
Instrumented Impact (0.5-in. dart, 3-in. clamp, 7.6 mph); Total Energy; ASTM-D3763 | |
| 15.0 J @Temperature -18.0 °C |
11.1 ft-lb @Temperature -0.400 °F |
Instrumented Impact (0.5-in. dart, 3-in. clamp, 7.6 mph); Peak Energy; ASTM-D3763 | |
| 16.0 J @Temperature -18.0 °C |
11.8 ft-lb @Temperature -0.400 °F |
Instrumented Impact (0.5-in. dart, 3-in. clamp, 7.6 mph); Total Energy; ASTM-D3763 | |
| 24.0 J @Temperature 23.0 °C |
17.7 ft-lb @Temperature 73.4 °F |
Instrumented Impact (0.5-in. dart, 3-in. clamp, 7.6 mph); Peak Energy; ASTM-D3763 | |
| 30.0 J @Temperature 23.0 °C |
22.1 ft-lb @Temperature 73.4 °F |
Instrumented Impact (0.5-in. dart, 3-in. clamp, 7.6 mph); Total Energy; ASTM-D3763 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 87.0 °C | 189 °F | Unannealed; ASTM-D648 |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Gloss | 25 % | 25 % | Formed, Angle 60°; ASTM-D523 |
| 90 % | 90 % | Sheet, Angle 60°; ASTM-D523 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Die Temperature | 210 - 241 °C | 410 - 466 °F | |
| Melt Temperature | 215 - 240 °C | 419 - 464 °F | Extruder |
| Roll Temperature | 47.0 °C | 117 °F | Down Stack, Middle |
| 82.0 °C | 180 °F | Up Stack, Bottom | |
| 88.0 °C | 190 °F | Up Stack, Middle | |
| 93.0 °C | 199 °F | Down Stack, Bottom | |
| 93.0 °C | 199 °F | Up Stack, Top | |
| 93.0 °C | 199 °F | Down Stack, Top | |
| Drying Temperature | 82.0 - 93.0 °C @Time 10800 - 14400 sec |
180 - 199 °F @Time 3.00 - 4.00 hour |
|
| Moisture Content | <= 0.030 % | <= 0.030 % | |
| Dew Point | <= -29.0 °C | <= -20.2 °F | inlet air |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Pump Ratio | 1.5-2.0 | Screw Design |
| Screw Compression Ratio | 2.5-2.7 |