- Ineos ABS Lustran® 248
Ineos ABS Lustran® 248
| Category | Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS), Molded |
| Manufacturer | Ineos ABS |
| Trade Name | Lustran® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Ineos ABS Lustran® 248.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Key Features:UnfilledSuitable processing methods:Injection molding
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.03 g/cc | 0.0372 lb/in³ | |
| Melt Flow | 17 g/10 min @Load 10.0 kg, Temperature 220 °C |
17 g/10 min @Load 22.0 lb, Temperature 428 °F |
cm³/10 min. |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 48.3 MPa | 7010 psi | |
| Elongation at Break | 25 % | 25 % | Nominal |
| Elongation at Yield | 3.6 % | 3.6 % | |
| Tensile Modulus | 2.49 GPa | 361 ksi | |
| Charpy Impact Unnotched | 8.70 J/cm² @Temperature -30.0 °C |
41.4 ft-lb/in² @Temperature -22.0 °F |
|
| Charpy Impact, Notched | 2.40 J/cm² | 11.4 ft-lb/in² | |
| 0.660 J/cm² @Temperature -30.0 °C |
3.14 ft-lb/in² @Temperature -22.0 °F |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 81.0 µm/m-°C @Temperature 20.0 °C |
45.0 µin/in-°F @Temperature 68.0 °F |
|
| Deflection Temperature at 0.46 MPa (66 psi) | 95.0 °C | 203 °F | |
| Deflection Temperature at 1.8 MPa (264 psi) | 85.0 °C | 185 °F | |
| Flammability, UL94 | HB @Thickness 1.50 mm |
HB @Thickness 0.0591 in |
UL Recognized |
| HB @Thickness 3.00 mm |
HB @Thickness 0.118 in |
UL Recognized |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 250 °C | 482 °F | Injection Molding |
| Mold Temperature | 60.0 °C | 140 °F | Injection Molding |
| Injection Velocity | 200 mm/sec | 7.87 in/sec | |
| Injection Pressure | 55.0 MPa | 7980 psi |
Users viewing this material also viewed the following:
- Precision Polymer Engineering S80Z Silicone Rubber
- Quadrant EPP TIVAR® 1000 UV Stabilized UHMW-PE, Natural & Colored Except Black (ASTM Product Data Sheet)
- Karina E 06/40-RG-PO Blue Color Concentrate for PVC
- Solvay Specialty Polymers Catalyst F/AC Polyolefin
- SABIC Innovative Plastics LNP THERMOCOMP RF006XXZ PA 66
- A. Schulman FORMION™ FI 389 Ionomer
- AlphaGary GW 2403-1 VW1 75 LCF Flame Retardant Polyvinyl Chloride
- AlphaGary GW 3040 LT LCF Flame Retardant Polyvinyl Chloride
- Samyang Triloy® 210N PC/ABS alloy, Flame Retardant
Copyright © lookpolymers.com All Rights Reserved