Ineos ABS Centrex® 813 ASA+AES Blend  (discontinued **)

Category Polymer , Thermoplastic , AES Polymer , ASA Polymer , Acrylonitrile/Styrene/Acrylate (ASA), Unreinforced, Molded
Manufacturer
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Ineos ABS Centrex® 813 ASA+AES Blend  (discontinued **).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Key Features:UnfilledHigh impact or high impact modifiedLight stabilized or stable to lightU.V. stabilized or stable to weatherSuitable processing methods:Injection moldingInformation provided by Bayer Polymers.LANXESS was spun-off from Bayer in early 2005. Business renamed Ineos ABS after INEOS acquires a majority shareholding under a JV with Lanxess in 2007. Subsequently Ineos acquired 100% of Ineos ABS.
Physical Properties Metric English Comments
Density 1.05 g/cc
0.0379 lb/in³
Melt Flow 7.9 g/10 min

@Load 10.0 kg,
Temperature 220 °C
7.9 g/10 min

@Load 22.0 lb,
Temperature 428 °F
cm³/10 min.
Mechanical Properties Metric English Comments
Tensile Strength, Yield 35.9 MPa
5210 psi
Elongation at Break 50 %
50 %
Nominal
Elongation at Yield 3.0 %
3.0 %
Tensile Modulus 1.87 GPa
271 ksi
Charpy Impact, Notched 4.36 J/cm²
20.8 ft-lb/in²
1.35 J/cm²

@Temperature -30.0 °C
6.42 ft-lb/in²

@Temperature -22.0 °F
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 121 µm/m-°C

@Temperature 20.0 °C
67.2 µin/in-°F

@Temperature 68.0 °F
Deflection Temperature at 0.46 MPa (66 psi) 89.0 °C
192 °F
Deflection Temperature at 1.8 MPa (264 psi) 77.0 °C
171 °F
Vicat Softening Point 93.0 °C
199 °F
50°C/h 50N
Flammability, UL94 HB

@Thickness 1.50 mm
HB

@Thickness 0.0591 in
UL Recognized
HB

@Thickness 3.00 mm
HB

@Thickness 0.118 in
UL Recognized
Processing Properties Metric English Comments
Melt Temperature 250 °C
482 °F
Injection Molding
Mold Temperature 60.0 °C
140 °F
Injection Molding
Injection Velocity 200 mm/sec
7.87 in/sec
Injection Pressure 60.0 MPa
8700 psi