Ineos ABS Cadon® 127 SMA General Purpose, High Heat  (discontinued **)

Category Polymer , Thermoplastic , SMA Polymer , Styrene-Maleic Anhydride (SMA), Heat Resistant
Manufacturer
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Ineos ABS Cadon® 127 SMA General Purpose, High Heat  (discontinued **).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Information provided by Bayer Corporation, Plastics DivisionLANXESS was spun-off from Bayer in early 2005. Business renamed Ineos ABS after INEOS acquires a majority shareholding under a JV with Lanxess in 2007. Subsequently Ineos acquired 100% of Ineos ABS. This product is no longer listed as a standard NAFTA product.
Physical Properties Metric English Comments
Density 1.07 g/cc
0.0387 lb/in³
ASTM D792
Linear Mold Shrinkage 0.0050 - 0.0070 cm/cm
0.0050 - 0.0070 in/in
ASTM D955
Melt Flow 2.0 g/10 min

@Load 3.80 kg,
Temperature 230 °C
2.0 g/10 min

@Load 8.38 lb,
Temperature 446 °F
ASTM D1238
Mechanical Properties Metric English Comments
Hardness, Rockwell R 104
104
ASTM D785
Tensile Strength, Yield 34.0 MPa
4930 psi
ASTM D638
Tensile Modulus 2.10 GPa
305 ksi
ASTM D638
Flexural Yield Strength 66.0 MPa
9570 psi
ASTM D790
Flexural Modulus 2.34 GPa
339 ksi
ASTM D790
Izod Impact, Notched 1.00 J/cm

@Temperature -40.0 °C
1.87 ft-lb/in

@Temperature -40.0 °F
ASTM D256
2.10 J/cm

@Thickness 3.17 mm
3.93 ft-lb/in

@Thickness 0.125 in
ASTM D256
Thermal Properties Metric English Comments
CTE, linear 70.0 µm/m-°C

@Temperature 20.0 °C
38.9 µin/in-°F

@Temperature 68.0 °F
ASTM D696
Deflection Temperature at 0.46 MPa (66 psi) 120 °C

@Thickness 13.0 mm
248 °F

@Thickness 0.512 in
ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 112 °C

@Thickness 13.0 mm
234 °F

@Thickness 0.512 in
ASTM D648
Vicat Softening Point 131 °C
268 °F
Rate B; ASTM D1525
UL RTI, Electrical 100 °C

@Thickness 1.60 mm
212 °F

@Thickness 0.0630 in
UL746B
UL RTI, Mechanical with Impact 95.0 °C

@Thickness 1.60 mm
203 °F

@Thickness 0.0630 in
UL746B
UL RTI, Mechanical without Impact 95.0 °C

@Thickness 1.60 mm
203 °F

@Thickness 0.0630 in
UL746B
Flammability, UL94 HB

@Thickness 1.57 mm
HB

@Thickness 0.0618 in
HB

@Thickness 1.57 mm
HB

@Thickness 0.0618 in
Processing Properties Metric English Comments
Melt Temperature 250 - 280 °C
482 - 536 °F