Industrial Laminates/Norplex NP511ES Glass Epoxy Laminate

Category Polymer , Thermoset
Manufacturer Industrial Laminates/Norplex
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Industrial Laminates/Norplex NP511ES Glass Epoxy Laminate.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Description: NP511ES is a woven glass fabric with high temperature, static dissipative epoxy resin. It has excellent mechanical strength and electrical properties at elevated temperatures with a continuous operating temperature of 165°C.
Physical Properties Metric English Comments
Specific Gravity 1.85 - 1.95 g/cc

@Thickness 1.57 mm
 1.85 - 1.95 g/cc

@Thickness 0.0620 in
 ASTM D792
Moisture Absorption at Equilibrium 0.22 %

@Thickness 1.57 mm
 0.22 %

@Thickness 0.0620 in
 ASTM D229
Mechanical Properties Metric English Comments
Hardness, Rockwell M 100 - 120

@Thickness 1.57 mm
 100 - 120

@Thickness 0.0620 in
 ASTM D785
Tensile Strength, Yield 331 MPa

@Thickness 1.57 mm
 48000 psi

@Thickness 0.0620 in
 CW; ASTM D638
415 MPa

@Thickness 1.57 mm
 60200 psi

@Thickness 0.0620 in
 LW; ASTM D638
Modulus of Elasticity 29.7 GPa

@Thickness 1.57 mm
 4310 ksi

@Thickness 0.0620 in
 CW; ASTM D229
33.0 GPa

@Thickness 1.57 mm
 4780 ksi

@Thickness 0.0620 in
 LW; ASTM D229
Flexural Strength 483 MPa

@Thickness 1.57 mm
 70000 psi

@Thickness 0.0620 in
 CW; ASTM D790
572 MPa

@Thickness 1.57 mm
 83000 psi

@Thickness 0.0620 in
 LW; ASTM D790
Compressive Strength 586 MPa

@Thickness 12.7 mm
 85000 psi

@Thickness 0.500 in
 ASTM D695
Shear Strength 179 MPa

@Thickness 15.7 mm
 26000 psi

@Thickness 0.620 in
 ASTM D732
Izod Impact, Unnotched 4.81 J/cm

@Thickness 12.7 mm
 9.00 ft-lb/in

@Thickness 0.500 in
 CW, Cond E-48/50; ASTM D256
6.94 J/cm

@Thickness 12.7 mm
 13.0 ft-lb/in

@Thickness 0.500 in
 LW, Cond E-48/50; ASTM D256
Thermal Properties Metric English Comments
CTE, linear 9.70 µm/m-°C

@Thickness 1.57 mm,
Temperature 20.0 °C
 5.39 µin/in-°F

@Thickness 0.0620 in,
Temperature 68.0 °F
 x-axis; IPC-TM 650-2.4.24
CTE, linear, Transverse to Flow 17.7 µm/m-°C

@Thickness 1.57 mm,
Temperature 20.0 °C
 9.83 µin/in-°F

@Thickness 0.0620 in,
Temperature 68.0 °F
 x-axis; IPC-TM 650-2.4.24
Maximum Service Temperature, Air 180 °C
356 °F
Glass Transition Temp, Tg 180 °C
356 °F
Tg
Flammability, UL94 HB

@Thickness 1.57 mm
 HB

@Thickness 0.0620 in
Descriptive Properties Value Comments
Bond Strength 1800 lb
0.5", ASTM D229
Color Black