Industrial Laminates/Norplex NP509 Glass Fabric

Category Polymer , Thermoset
Manufacturer Industrial Laminates/Norplex
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Industrial Laminates/Norplex NP509 Glass Fabric.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Description: Woven glass fabric, melamine resin laminate. Very hard, flame resistant, machining grade with excellent electrical properties in high humidity conditions. High physical strength and excellent arc resistance. Meets U.L. flammability classification V-0. MIL-P-24768/1 & 8, types GMG & GME.Thickness Tested: 0.062", 0.125" and 0.500"
Physical Properties Metric English Comments
Specific Gravity 1.80 - 1.90 g/cc

@Thickness 1.57 mm
 1.80 - 1.90 g/cc

@Thickness 0.0620 in
 ASTM D792
Moisture Absorption at Equilibrium 0.60 %

@Thickness 1.57 mm
 0.60 %

@Thickness 0.0620 in
 ASTM D229
Mechanical Properties Metric English Comments
Hardness, Rockwell M 105 - 125

@Thickness 1.57 mm
 105 - 125

@Thickness 0.0620 in
 ASTM D785
Tensile Strength, Yield 352 MPa

@Thickness 1.57 mm
 51100 psi

@Thickness 0.0620 in
 CW; ASTM D638
425 MPa

@Thickness 1.57 mm
 61600 psi

@Thickness 0.0620 in
 LW; ASTM D638
Modulus of Elasticity 11.7 GPa

@Thickness 1.57 mm
 1700 ksi

@Thickness 0.0620 in
 CW; ASTM D229
13.8 GPa

@Thickness 1.57 mm
 2000 ksi

@Thickness 0.0620 in
 LW; ASTM D229
Flexural Strength 352 MPa

@Thickness 1.57 mm
 51100 psi

@Thickness 0.0620 in
 CW; ASTM D790
425 MPa

@Thickness 1.57 mm
 61600 psi

@Thickness 0.0620 in
 LW; ASTM D790
Compressive Strength 483 MPa

@Thickness 12.7 mm
 70000 psi

@Thickness 0.500 in
 ASTM D695
Shear Strength 124 MPa

@Thickness 15.7 mm
 18000 psi

@Thickness 0.620 in
 ASTM D732
Izod Impact, Unnotched 4.54 J/cm

@Thickness 12.7 mm
 8.50 ft-lb/in

@Thickness 0.500 in
 CW, Cond E-48/50; ASTM D256
6.67 J/cm

@Thickness 12.7 mm
 12.5 ft-lb/in

@Thickness 0.500 in
 LW, Cond E-48/50; ASTM D256
Thermal Properties Metric English Comments
CTE, linear 15.0 µm/m-°C

@Thickness 1.57 mm,
Temperature 20.0 °C
 8.33 µin/in-°F

@Thickness 0.0620 in,
Temperature 68.0 °F
 x-axis; IPC-TM 650-2.4.24
CTE, linear, Transverse to Flow 18.0 µm/m-°C

@Thickness 1.57 mm,
Temperature 20.0 °C
 10.0 µin/in-°F

@Thickness 0.0620 in,
Temperature 68.0 °F
 x-axis; IPC-TM 650-2.4.24
Maximum Service Temperature, Air 140 °C
284 °F
Flammability, UL94 V-0

@Thickness 1.57 mm
 V-0

@Thickness 0.0620 in
Electrical Properties Metric English Comments
Dielectric Constant 7.03

@Thickness 1.57 mm
 7.03

@Thickness 0.0620 in
 Permittivity, Cond D-24/23; ASTM D150
Dielectric Strength 15.7 kV/mm

@Thickness 1.57 mm
 400 kV/in

@Thickness 0.0620 in
 Cond D-48/50; ASTM D229 S.T.
17.7 kV/mm

@Thickness 1.57 mm
 450 kV/in

@Thickness 0.0620 in
 Cond A; ASTM D229 S.T.
Dielectric Breakdown 55000 V

@Thickness 1.57 mm
 55000 V

@Thickness 0.0620 in
 Cond D-48/50; ASTM D229 S/S
65000 V

@Thickness 1.57 mm
 65000 V

@Thickness 0.0620 in
 Cond A; ASTM D229 S/S
Dissipation Factor 0.15

@Thickness 1.57 mm
 0.15

@Thickness 0.0620 in
 Cond D-24/23; ASTM D150
Arc Resistance 185 sec

@Thickness 3.17 mm
 185 sec

@Thickness 0.125 in
 ASTM D495
Comparative Tracking Index >= 600 V

@Thickness 3.17 mm
 >= 600 V

@Thickness 0.125 in
 ASTM D3638
Descriptive Properties Value Comments
Bond Strength 1900 lb
0.5", ASTM D229
Color Natural
Users viewing this material also viewed the following: