Industrial Laminates/Norplex MC514MG Glass Fabric

Category Polymer , Thermoset , Phenolic
Manufacturer Industrial Laminates/Norplex
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Industrial Laminates/Norplex MC514MG Glass Fabric.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Description: MC514MG is made with a woven glass fabric in combination with high temperature, conductive, phenolic resin system.NP514MG has excellent flexural, compressive and impact strengths at room temperature and elevated temperatures. It was developed for the motor generator industry to provide conductive coupling to eliminate static discharges caused by corona. It is capable of continuous operation exceeding 300°C.NP514MG has excellent creep resistance because of the phenolic resin system.Thickness Tested: 0.062”, 0.125”, and 0.500”
Physical Properties Metric English Comments
Specific Gravity 1.85 g/cc
1.85 g/cc
Moisture Absorption at Equilibrium 0.70 %

@Thickness 1.57 mm
 0.70 %

@Thickness 0.0620 in
Mechanical Properties Metric English Comments
Hardness, Rockwell M 105 - 125

@Thickness 1.57 mm
 105 - 125

@Thickness 0.0620 in
Tensile Strength, Yield 255 MPa

@Thickness 3.17 mm
 37000 psi

@Thickness 0.125 in
 CW
317 MPa

@Thickness 3.17 mm
 46000 psi

@Thickness 0.125 in
 LW
Flexural Strength 379 MPa

@Thickness 1.57 mm
 55000 psi

@Thickness 0.0620 in
 CW
441 MPa

@Thickness 1.57 mm
 64000 psi

@Thickness 0.0620 in
 LW
Flexural Modulus 25.5 GPa

@Thickness 1.57 mm
 3700 ksi

@Thickness 0.0620 in
 CW
27.6 GPa

@Thickness 1.57 mm
 4000 ksi

@Thickness 0.0620 in
 LW
Compressive Strength 455 MPa

@Thickness 12.7 mm
 66000 psi

@Thickness 0.500 in
 Flatwise
Shear Strength 172 MPa

@Thickness 1.57 mm
 25000 psi

@Thickness 0.0620 in
 Perpendicular
Izod Impact, Notched 5.87 J/cm

@Thickness 12.7 mm
 11.0 ft-lb/in

@Thickness 0.500 in
 CW, E-48/50
6.94 J/cm

@Thickness 12.7 mm
 13.0 ft-lb/in

@Thickness 0.500 in
 LW, E-48/50
Thermal Properties Metric English Comments
Maximum Service Temperature, Air 300 °C
572 °F
Decomposition Temperature >= 385 °C
>= 725 °F
Degradation Temperature
Flammability, UL94 HB
HB
Descriptive Properties Value Comments
Bond Strength 1,600 lb
0.5"
Conductivity Range Surface 104ohm/Square
Preliminary
Glass Transition Temperature None