- Industeel URANUS® 47N+ 25 Cr Super Duplex Stainless Steel with PREN = 40
Industeel URANUS® 47N+ 25 Cr Super Duplex Stainless Steel with PREN = 40
| Category | Metal , Ferrous Metal , Duplex , Stainless Steel , T S30000 Series Stainless Steel |
| Manufacturer | Groupe Arcelor |
| Trade Name | URANUS® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Industeel URANUS® 47N+ 25 Cr Super Duplex Stainless Steel with PREN = 40.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description: CLI - SAF 2507® is a 25.07 super duplex stainless steel with 25% Cr and a PREN value higher than 40. The minimum guaranteed yield strength is 550 MPa which allows the designer to reduce weight. The molybdenum and nitrogen additions have been optimized in order to obtain the best corrosion resistance properties even for heavy plates. Its high nitrogen content improves the structure stability particularly in HAZ. The CLI - SAF 2507® (URANUS® 47N+) grade is an overalloyed variant of the former UR 47N grade of CLI. CLI - SAF 2507® has improved corrosion resistance properties when compared to duplex 2205 type materials, or even to URANUS® 47N. It is designed for service in severe corrosive conditions. The alloy is particularly resistant to stress corrosion cracking and crevice corrosion. CLI - SAF 2507® is a cost efficient grade designed for Oil & Gas industry, Seawater applications, Desalination plants, Geothermal wells or Refineries and Petrochemical plants.Information provided by manufacturer.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 7.82 g/cc | 0.283 lb/in³ |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell C | <= 28 | <= 28 | Typical |
| Hardness, Vickers | 250 - 280 | 250 - 280 | Typical, V<sub>5</sub> |
| Tensile Strength, Ultimate | >= 770 MPa | >= 112000 psi | |
| Tensile Strength, Yield | >= 550 MPa @Strain 0.200 % |
>= 79800 psi @Strain 0.200 % |
|
| >= 570 MPa @Strain 1.00 % |
>= 82700 psi @Strain 1.00 % |
||
| Elongation at Break | >= 25 % | >= 25 % | |
| Modulus of Elasticity | 200 GPa | 29000 ksi | |
| Poissons Ratio | 0.333 | 0.333 | Calculated |
| Shear Modulus | 75.0 GPa @Temperature 20.0 °C |
10900 ksi @Temperature 68.0 °F |
|
| Charpy Impact | >= 95.0 J | >= 70.1 ft-lb | |
| >= 70.0 J @Temperature -50.0 °C |
>= 51.6 ft-lb @Temperature -58.0 °F |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 13.5 µm/m-°C @Temperature 20.0 - 100 °C |
7.50 µin/in-°F @Temperature 68.0 - 212 °F |
|
| 14.0 µm/m-°C @Temperature 20.0 - 200 °C |
7.78 µin/in-°F @Temperature 68.0 - 392 °F |
||
| 14.5 µm/m-°C @Temperature 20.0 - 300 °C |
8.06 µin/in-°F @Temperature 68.0 - 572 °F |
||
| Specific Heat Capacity | 0.450 J/g-°C @Temperature 20.0 °C |
0.108 BTU/lb-°F @Temperature 68.0 °F |
|
| Thermal Conductivity | 17.0 W/m-K @Temperature 20.0 °C |
118 BTU-in/hr-ft²-°F @Temperature 68.0 °F |
| Component Elements Properties | Metric | English | Comments |
|---|---|---|---|
| Carbon, C | <= 0.030 % | <= 0.030 % | |
| Chromium, Cr | 25 % | 25 % | |
| Iron, Fe | 64.61 - 64.64 % | 64.61 - 64.64 % | As remainder |
| Molybdenum, Mo | 3.6 % | 3.6 % | |
| Nickel, Ni | 6.5 % | 6.5 % | |
| Nitrogen, N | 0.26 % | 0.26 % |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Electrical Resistivity | 0.0000850 ohm-cm @Temperature 20.0 °C |
0.0000850 ohm-cm @Temperature 68.0 °F |