- Industeel CLC 18.10 Nb Niobium Stabilized 18Cr-10Ni Austenitic Stainless Steel
Industeel CLC 18.10 Nb Niobium Stabilized 18Cr-10Ni Austenitic Stainless Steel
| Category | Metal , Ferrous Metal , Austenitic , Stainless Steel , T S30000 Series Stainless Steel |
| Manufacturer | Groupe Arcelor |
| Trade Name | CLC |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Industeel CLC 18.10 Nb Niobium Stabilized 18Cr-10Ni Austenitic Stainless Steel.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
CLC 18-10Nb is a 18Cr-10Ni austenitic stainless steel stabilized with specific Nb addition. This kind of steel is one of the basic grades of the stainless steels range. Niobium bearing and its low carbon content ensure better ductility and avoid the intergranular corrosion, even on welded pieces without ulterior water quenching. Alloys CLC 18-10Nb exhibit austenitic microstructures free of deleterious carbide precipitations at grain boundaries. The grade contain some residual ferrite (~ 3%) after solution annealing (1000-1100°C – 1832-2012°F) and water quenching. The main properties of CLC 18-10Nb are :basic corrosion resistanceresistance against intergranular corrosionhigh ductilitymedium temperature applicationTensile properties after water quenching.Information provided by manufacturer.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 7.95 g/cc | 0.287 lb/in³ |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Ultimate | 520 MPa | 75400 psi | |
| Tensile Strength, Yield | >= 200 MPa @Strain 0.200 % |
>= 29000 psi @Strain 0.200 % |
|
| >= 240 MPa @Strain 1.00 % |
>= 34800 psi @Strain 1.00 % |
||
| Elongation at Break | 40 % | 40 % | |
| Creep Strength | 210 MPa @Temperature 600 °C, Time 3.60e+6 sec |
30500 psi @Temperature 1110 °F, Time 1000 hour |
|
| Modulus of Elasticity | 200 GPa @Temperature 20.0 - 100 °C |
29000 ksi @Temperature 68.0 - 212 °F |
|
| Poissons Ratio | 0.299 | 0.299 | Calculated |
| Shear Modulus | 77.0 GPa @Temperature 20.0 - 100 °C |
11200 ksi @Temperature 68.0 - 212 °F |
|
| Charpy Impact | >= 150 J | >= 111 ft-lb | |
| 225 J | 166 ft-lb | Typical | |
| >= 100 J @Temperature -196 °C |
>= 73.8 ft-lb @Temperature -321 °F |
||
| 175 J @Temperature -196 °C |
129 ft-lb @Temperature -321 °F |
Typical |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 16.0 µm/m-°C @Temperature 20.0 - 100 °C |
8.89 µin/in-°F @Temperature 68.0 - 212 °F |
|
| 16.5 µm/m-°C @Temperature 20.0 - 200 °C |
9.17 µin/in-°F @Temperature 68.0 - 392 °F |
||
| 17.0 µm/m-°C @Temperature 20.0 - 300 °C |
9.44 µin/in-°F @Temperature 68.0 - 572 °F |
||
| 18.0 µm/m-°C @Temperature 20.0 - 500 °C |
10.0 µin/in-°F @Temperature 68.0 - 932 °F |
||
| Specific Heat Capacity | 0.500 J/g-°C @Temperature 20.0 - 100 °C |
0.120 BTU/lb-°F @Temperature 68.0 - 212 °F |
|
| Thermal Conductivity | 15.0 W/m-K @Temperature 20.0 - 100 °C |
104 BTU-in/hr-ft²-°F @Temperature 68.0 - 212 °F |
| Component Elements Properties | Metric | English | Comments |
|---|---|---|---|
| Carbon, C | 0.030 % | 0.030 % | |
| Chromium, Cr | 17.5 % | 17.5 % | |
| Iron, Fe | 72.27 - 73.03 % | 72.27 - 73.03 % | As remainder |
| Nickel, Ni | 9.2 % | 9.2 % | |
| Titanium, Ti | 0.24 - 1.0 % | 0.24 - 1.0 % |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Electrical Resistivity | 0.0000730 ohm-cm @Temperature 20.0 - 100 °C |
0.0000730 ohm-cm @Temperature 68.0 - 212 °F |