IRPC Polimaxx Porene KU200 Acrylonitrile Butadiene Styrene

Category Polymer , Thermoplastic , ABS Polymer
Manufacturer IRPC Polimaxx
Trade Name Porene
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF IRPC Polimaxx Porene KU200 Acrylonitrile Butadiene Styrene.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Applications:extrusion applicationautomotive parts such as instrument panels, console boxes, switches, automotive louvers, ectelectrical appliances
Physical Properties Metric English Comments
Melt Flow 6.0 g/10 min

@Load 10.0 kg,
Temperature 220 °C
 6.0 g/10 min

@Load 22.0 lb,
Temperature 428 °F
 ASTM D1238
Mechanical Properties Metric English Comments
Hardness, Rockwell R 110

@Thickness 6.35 mm,
Temperature 23.0 °C
 110

@Thickness 0.250 in,
Temperature 73.4 °F
 ASTM D785
Tensile Strength, Ultimate 48.1 MPa

@Temperature 23.0 °C
 6970 psi

@Temperature 73.4 °F
 ASTM D638
Elongation at Break 25 %

@Temperature 23.0 °C
 25 %

@Temperature 73.4 °F
 ASTM D638
Flexural Yield Strength 64.7 MPa

@Temperature 23.0 °C
 9390 psi

@Temperature 73.4 °F
 ASTM D790
Flexural Modulus 2.16 GPa

@Temperature 23.0 °C
 313 ksi

@Temperature 73.4 °F
 ASTM D790
Izod Impact, Notched 2.06 J/cm

@Thickness 6.35 mm,
Temperature 23.0 °C
 3.86 ft-lb/in

@Thickness 0.250 in,
Temperature 73.4 °F
 ASTM D256
Thermal Properties Metric English Comments
Deflection Temperature at 1.8 MPa (264 psi) 97.0 °C

@Thickness 6.35 mm
 207 °F

@Thickness 0.250 in
 ASTM D648
Flammability, UL94 HB

@Thickness 1.50 mm
 HB

@Thickness 0.0591 in
Processing Properties Metric English Comments
Processing Temperature 220 - 270 °C
428 - 518 °F
Drying Temperature 85.0 - 95.0 °C

@Time 7200 - 18000 sec
 185 - 203 °F

@Time 2.00 - 5.00 hour