- IDI Composites M-102 Thermoset Polyester, Molding
IDI Composites M-102 Thermoset Polyester, Molding
| Category | Polymer , Thermoset , Polyester, TS , Thermoset Polyester Glass Filled BMC |
| Manufacturer | IDI Composites |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | IDI Composites M-102 Thermoset Polyester, Molding.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Mechanical grade materials in a range of strengths with excellent moldability and molded part appearance.Data provided by the manufacturer.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.89 g/cc | 0.0683 lb/in³ | |
| Water Absorption | 0.090 % | 0.090 % | in 24 hours; ASTM D570 |
| Linear Mold Shrinkage | 0.0020 cm/cm | 0.0020 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Ultimate | 48.0 MPa | 6960 psi | ASTM D638 |
| Flexural Strength | 83.0 MPa | 12000 psi | ASTM D790 |
| Flexural Modulus | 9.00 GPa | 1310 ksi | ASTM D790 |
| Compressive Strength | 152 MPa | 22000 psi | ASTM D695 |
| Izod Impact, Notched | 1.90 J/cm | 3.56 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 232 °C | 450 °F | ASTM D648 |
| Flammability, UL94 | V-2 @Thickness 3.20 mm |
V-2 @Thickness 0.126 in |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Dielectric Strength | 12.6 kV/mm | 320 kV/in | ASTM D149 |