- Low Density Polyethylene (LDPE), Masterbatch Grade
- ICO Polymers ICOTEXâ„¢ 520-5019 300 Micron LDPE Powder
ICO Polymers ICOTEXâ„¢ 520-5019 300 Micron LDPE Powder
| Category | Polymer , Thermoplastic , Polyethylene (PE) , LDPE , Low Density Polyethylene (LDPE), Masterbatch Grade |
| Manufacturer | ICO Polymers (A Schulman Inc.) |
| Trade Name | ICOTEX™ |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | ICO Polymers ICOTEXâ„¢ 520-5019 300 Micron LDPE Powder.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description: ICOTEX 520-5019 is a low density polyethylene powder that has been developed to meet the special requirements of the textile coating industry. Key Characteristics: good melt flow and a very fine powder that enables fast and accurate melting. Information provided by ICO Polymers.A Schulman acquired ICO, Inc. in 2010.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.913 g/cc | 0.0330 lb/in³ | ASTM D1505 |
| Particle Size | >= 150 µm | >= 150 µm | pan, 9% |
| <= 300 µm | <= 300 µm | sieve < 5% | |
| Melt Index of Compound | 70 g/10 min @Load 2.16 kg, Temperature 190 °C |
70 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 8.00 MPa | 1160 psi | ASTM D638 |
| Tensile Strength, Yield | 8.00 MPa | 1160 psi | 50 mm/min; ASTM D638 |
| Elongation at Break | 100 % | 100 % | 50 mm/min; ASTM D638 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 100 °C | 212 °F | DSC; ASTM D3418 |
| 130 °C | 266 °F | fusing temperature | |
| Vicat Softening Point | 75.0 °C | 167 °F | ASTM D1525 |
| Brittleness Temperature | -25.0 °C | -13.0 °F | ASTM D638 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Max Dry Flow | max 37 sec/100g | ASTM |