Hyosung Topilene B240T PP
| Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene, Impact Modified; Molded/Extruded |
| Manufacturer | Hyosung Co. |
| Trade Name | Topilene |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Hyosung Topilene B240T PP.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
B240T Extrusion Impact CopolymerApplications:Thermoforming sheetStationary sheetCharacteristics:High impactHigh stiffnessInformation provided by Hyosung Corporation
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Flow | 0.50 g/10 min | 0.50 g/10 min | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 70 | 70 | ASTM D785 |
| Tensile Strength, Yield | 29.4 MPa | 4270 psi | ASTM D638 |
| Elongation at Break | 500 % | 500 % | ASTM D638 |
| Flexural Modulus | 1.32 GPa | 192 ksi | ASTM D790 |
| Izod Impact, Unnotched | NB | NB | ASTM D256 |
| 0.637 J/cm @Temperature -10.0 °C |
1.19 ft-lb/in @Temperature 14.0 °F |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 110 °C | 230 °F | ASTM D648 |
| Vicat Softening Point | 150 °C | 302 °F | ASTM D1525 |
Users viewing this material also viewed the following:
- Owens Corning Glass Fiber Reinforced Polyester (PBT), 30 wt.% glass
- Lanxess Pocan® C 3230 XF 000000 PBT + PC, 30% Glass Fiber
- Silikony Polskie Polsil OM 10 Methyl Silicone Fluid
- UBE UBEPOL BR15HL HIPS (n-DM = 0.03 wt % and PH-3H = 0.03 wt %)
- Lubrizol Estane® ALR PC73A Thermoplastic Polyurethane
- Cossa Polimeri ESTASTIR HI 1012 Polystyrene
- Dow Tyril® 1011 SAN
- Ashley Polymers Ashlene® 990L-30G Nylon 610, 30% Glass Reinforced
- DSM Akulon® K-FHG0 (Cond.) 50% Glass Reinforced Nylon 6 (North America) (discontinued **)
Copyright © lookpolymers.com All Rights Reserved