Huntsman Rexell® V8801 Cast Film Extrusion LLDPE  (discontinued **)

Category Polymer , Film , Thermoplastic , Polyethylene (PE) , LLDPE , Linear Low Density Polyethylene (LLDPE), Film Grade
Manufacturer
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Huntsman Rexell® V8801 Cast Film Extrusion LLDPE  (discontinued **).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Linear-low very low density copolymer, blown film extrusion, FDA compliantFeatures: Excellent resistance to impact, puncturing, tearing, and flex cracking with good weld seal strength, hot tack, and sealability through contaminated surfaces.Applications: Medical and dental applications. Superior performance for fractional gauge application.Film properties based on 1.0 guage (25 µm) thickness; blow-up ratio 2:1.Information provided by Huntsman Corporation
Physical Properties Metric English Comments
Density 0.913 g/cc
0.0330 lb/in³
ASTM D1505
Thickness 25.4 microns
1.00 mil
Melt Flow 1.0 g/10 min
1.0 g/10 min
ASTM D1238
Mechanical Properties Metric English Comments
Film Elongation at Break, MD 530 %
530 %
ASTM D882
Film Elongation at Break, TD >= 700 %
>= 700 %
ASTM D882
Secant Modulus, MD 0.131 GPa
19.0 ksi
ASTM D882
Secant Modulus, TD 0.152 GPa
22.0 ksi
ASTM D882
Elmendorf Tear Strength MD 400 g
400 g
ASTM D1922
Elmendorf Tear Strength TD 760 g
760 g
ASTM D1922
Elmendorf Tear Strength, MD 15.7 g/micron
400 g/mil
ASTM D1922
Elmendorf Tear Strength, TD 29.9 g/micron
760 g/mil
ASTM D1922
Dart Drop 15.7 g/micron
400 g/mil
ASTM D1709
Dart Drop Test 400 g
0.882 lb
ASTM D1709
Film Tensile Strength at Break, MD 37.0 MPa
5370 psi
ASTM D882
Film Tensile Strength at Break, TD >= 20.0 MPa
>= 2900 psi
ASTM D882
Optical Properties Metric English Comments
Haze 6.0 %
6.0 %
ASTM D1003
Gloss 73 %
73 %
at 45°; ASTM D523
Processing Properties Metric English Comments
Melt Temperature 205 - 245 °C
401 - 473 °F