Huntsman Rexell® V3401 Blown Film Extrusion LLDPE (discontinued **)

Category	Polymer , Film , Thermoplastic , Polyethylene (PE) , LLDPE , Linear Low Density Polyethylene (LLDPE), Film Grade
Manufacturer
Trade Name
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Huntsman Rexell® V3401 Blown Film Extrusion LLDPE (discontinued **).pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Ultra linear low density copolymer, cast film extrusion, FDA compliant.Features: Excellent processability, toughness, and optics with good sealing properties.Applications: Sealing layer in coextruded packaging films.FDA Notes: Conforms to FDA regulation 21 CFR 177.1520 (c)3.1.b.Film properties based on 1.0 guage (25 µm) thickness; blow-up ratio 2:1.Information provided by Huntsman Corporation

Physical Properties	Metric	English	Comments
Density	0.910 g/cc	0.0329 lb/in³	ASTM D1505
Thickness	25.4 microns	1.00 mil
Melt Flow	6.6 g/10 min	6.6 g/10 min	ASTM D1238

Mechanical Properties	Metric	English	Comments
Film Elongation at Break, MD	520 %	520 %	ASTM D882
Film Elongation at Break, TD	>= 700 %	>= 700 %	ASTM D882
Secant Modulus, MD	0.0760 GPa	11.0 ksi	ASTM D882
Secant Modulus, TD	0.0760 GPa	11.0 ksi	ASTM D882
Elmendorf Tear Strength MD	350 g	350 g	ASTM D1922
Elmendorf Tear Strength TD	530 g	530 g	ASTM D1922
Elmendorf Tear Strength, MD	13.8 g/micron	350 g/mil	ASTM D1922
Elmendorf Tear Strength, TD	20.9 g/micron	530 g/mil	ASTM D1922
Dart Drop	8.19 g/micron	208 g/mil	ASTM D1709
Dart Drop Test	208 g	0.459 lb	ASTM D1709
Film Tensile Strength at Break, MD	29.0 MPa	4210 psi	ASTM D882
Film Tensile Strength at Break, TD	14.0 MPa	2030 psi	ASTM D882

Optical Properties	Metric	English	Comments
Haze	1.0 %	1.0 %	ASTM D1003
Gloss	50 %	50 %	at 45°; ASTM D523

Processing Properties	Metric	English	Comments
Melt Temperature	260 - 290 °C	500 - 554 °F