Huntsman Rexell® M3105 Blown Film Extrusion LLDPE  (discontinued **)

Category Polymer , Film , Thermoplastic , Polyethylene (PE) , LLDPE , Linear Low Density Polyethylene (LLDPE), Film Grade
Manufacturer
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Huntsman Rexell® M3105 Blown Film Extrusion LLDPE  (discontinued **).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Linear-low medium density copolymer, cast film extrusion, FDA compliantFeatures: Excellent combination of toughness, stiffness, and water vapor barrier with good temperature resistance.Applications: Diaper films, wrapping film, laminated films, and coextruded films for sterility in food and medical applications.FDA Notes: Conforms to FDA regulation 21 CFR 177.1520 (c)3.2.aFilm properties based on 1.0 guage (25 µm) thickness; blow-up ratio 2:1.Information provided by Huntsman Corporation
Physical Properties Metric English Comments
Density 0.936 g/cc
0.0338 lb/in³
ASTM D1505
Thickness 25.4 microns
1.00 mil
Melt Flow 2.2 g/10 min
2.2 g/10 min
ASTM D1238
Mechanical Properties Metric English Comments
Film Elongation at Break, MD 470 %
470 %
ASTM D882
Film Elongation at Break, TD >= 700 %
>= 700 %
ASTM D882
Secant Modulus, MD 0.300 GPa
43.5 ksi
ASTM D882
Secant Modulus, TD 0.340 GPa
49.3 ksi
ASTM D882
Elmendorf Tear Strength MD 43 g
43 g
ASTM D1922
Elmendorf Tear Strength TD 760 g
760 g
ASTM D1922
Elmendorf Tear Strength, MD 1.69 g/micron
43.0 g/mil
ASTM D1922
Elmendorf Tear Strength, TD 29.9 g/micron
760 g/mil
ASTM D1922
Dart Drop 2.52 g/micron
64.0 g/mil
ASTM D1709
Dart Drop Test 64.0 g
0.141 lb
ASTM D1709
Film Tensile Strength at Break, MD 50.0 MPa
7250 psi
ASTM D882
Film Tensile Strength at Break, TD 19.0 MPa
2760 psi
ASTM D882
Optical Properties Metric English Comments
Haze 2.6 %
2.6 %
ASTM D1003
Gloss 91 %
91 %
at 45°; ASTM D523
Processing Properties Metric English Comments
Melt Temperature 260 - 290 °C
500 - 554 °F