Huntsman Rexell® M3104 Blown Film Extrusion LLDPE  (discontinued **)

Category Polymer , Film , Thermoplastic , Polyethylene (PE) , LLDPE , Linear Low Density Polyethylene (LLDPE), Film Grade
Manufacturer
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Huntsman Rexell® M3104 Blown Film Extrusion LLDPE  (discontinued **).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Linear-low medium density copolymer, cast film extrusion, FDA compliant.Features: Excellent combination of toughness, stiffness, and optics with good temperature resistance.Applications: Diaper films, wrapping film, laminated films, and coextruded films for sterility in food and medical applications.FDA Notes: Conforms to FDA regulation 21 CFR 177.1520 (c)3.2.aFilm properties based on 1.0 guage (25 µm) thickness; blow-up ratio 2:1.Information provided by Huntsman Corporation
Physical Properties Metric English Comments
Density 0.932 g/cc
0.0337 lb/in³
ASTM D1505
Thickness 25.4 microns
1.00 mil
Melt Flow 2.2 g/10 min
2.2 g/10 min
ASTM D1238
Mechanical Properties Metric English Comments
Film Elongation at Break, MD 490 %
490 %
ASTM D882
Film Elongation at Break, TD >= 700 %
>= 700 %
ASTM D882
Secant Modulus, MD 0.255 GPa
37.0 ksi
ASTM D882
Secant Modulus, TD 0.297 GPa
43.1 ksi
ASTM D882
Elmendorf Tear Strength MD 58 g
58 g
ASTM D1922
Elmendorf Tear Strength TD 710 g
710 g
ASTM D1922
Elmendorf Tear Strength, MD 2.28 g/micron
58.0 g/mil
ASTM D1922
Elmendorf Tear Strength, TD 28.0 g/micron
710 g/mil
ASTM D1922
Dart Drop 3.54 g/micron
90.0 g/mil
ASTM D1709
Dart Drop Test 90.0 g
0.198 lb
ASTM D1709
Film Tensile Strength at Break, MD 46.0 MPa
6670 psi
ASTM D882
Film Tensile Strength at Break, TD 21.0 MPa
3050 psi
ASTM D882
Optical Properties Metric English Comments
Haze 2.2 %
2.2 %
ASTM D1003
Gloss 90 %
90 %
at 45°; ASTM D523
Processing Properties Metric English Comments
Melt Temperature 260 - 290 °C
500 - 554 °F