Huntsman Rexell® L8404 Cast Film Extrusion LLDPE (discontinued **)

Category	Polymer , Film , Thermoplastic , Polyethylene (PE) , LLDPE , Linear Low Density Polyethylene (LLDPE), Film Grade
Manufacturer
Trade Name
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Huntsman Rexell® L8404 Cast Film Extrusion LLDPE (discontinued **).pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Linear-low density copolymer, and FDA compliant.Applications: Blown film extrusion: general purpose.Film properties based on 1.0 guage (25 µm) thickness; blow-up ratio 2:1.Information provided by Huntsman Corporation

Physical Properties	Metric	English	Comments
Density	0.926 g/cc	0.0335 lb/in³	ASTM D1505
Thickness	25.4 microns	1.00 mil
Melt Flow	1.0 g/10 min	1.0 g/10 min	ASTM D1238

Mechanical Properties	Metric	English	Comments
Film Elongation at Break, MD	620 %	620 %	ASTM D882
Film Elongation at Break, TD	870 %	870 %	ASTM D882
Secant Modulus, MD	0.248 GPa	36.0 ksi	ASTM D882
Secant Modulus, TD	0.324 GPa	47.0 ksi	ASTM D882
Elmendorf Tear Strength MD	270 g	270 g	ASTM D1922
Elmendorf Tear Strength TD	660 g	660 g	ASTM D1922
Elmendorf Tear Strength, MD	10.6 g/micron	270 g/mil	ASTM D1922
Elmendorf Tear Strength, TD	26.0 g/micron	660 g/mil	ASTM D1922
Dart Drop	5.28 g/micron	134 g/mil	ASTM D1709
Dart Drop Test	134 g	0.295 lb	ASTM D1709
Film Tensile Strength at Break, MD	53.0 MPa	7690 psi	ASTM D882
Film Tensile Strength at Break, TD	45.0 MPa	6530 psi	ASTM D882

Optical Properties	Metric	English	Comments
Haze	7.0 %	7.0 %	ASTM D1003
Gloss	75 %	75 %	at 45°; ASTM D523

Processing Properties	Metric	English	Comments
Melt Temperature	205 - 245 °C	401 - 473 °F