Huntsman PE5020 Extrusion Coating Polyethylene  (discontinued **)

Category Polymer , Film , Thermoplastic , Polyethylene (PE) , LDPE , Low Density Polyethylene (LDPE), Extrusion Grade
Manufacturer
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Huntsman PE5020 Extrusion Coating Polyethylene  (discontinued **).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Homopolymer and FDA compliant.Features: High draw down, low neck-in, excellent heat sealability, and excellent adhesion.Applications: Extrusion: coating grade and thin coatings.FDA Notes: Conforms to FDA regulation 21 CFR 177.1520 (c)2.2 under condition of use B through H described in Table 2 of 21 CFR 176.170Film properties based on 1.0 guage (25 µm) thickness; blow-up ratio 2:1.Information provided by Huntsman Corporation
Physical Properties Metric English Comments
Density 0.917 g/cc
0.0331 lb/in³
ASTM D1505
Melt Flow 4.0 g/10 min
4.0 g/10 min
ASTM D1238
Mechanical Properties Metric English Comments
Hardness, Shore D 45
45
ASTM D2240
Tensile Strength, Ultimate 12.0 MPa
1740 psi
ASTM D638
Tensile Strength, Yield 11.0 MPa
1600 psi
ASTM D638
Film Elongation at Break, MD 280 %
280 %
ASTM D882
Film Elongation at Break, TD 420 %
420 %
ASTM D882
Elongation at Break 500 %
500 %
ASTM D638
Modulus of Elasticity 0.173 GPa
25.1 ksi
Secant; ASTM D638
Secant Modulus, MD 0.104 GPa
15.1 ksi
ASTM D882
Secant Modulus, TD 0.138 GPa
20.0 ksi
ASTM D882
Film Tensile Strength at Break, MD 18.0 MPa
2610 psi
ASTM D882
Film Tensile Strength at Break, TD 16.0 MPa
2320 psi
ASTM D882
Thermal Properties Metric English Comments
Vicat Softening Point 90.0 °C
194 °F
ASTM D1525
Processing Properties Metric English Comments
Melt Temperature 249 - 288 °C
480 - 550 °F