Songhan Plastic Technology Co.,Ltd.
 POLYMER SEARCH

Huntsman PE1651 EVA Film Extrusion  (discontinued **)

Category Polymer , Film , Thermoplastic , Ethylene Vinyl Acetate , Ethylene Vinyl Acetate Copolymer (EVA), Film Grade
Manufacturer
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Huntsman PE1651 EVA Film Extrusion  (discontinued **).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
6.5% Vinyl Acetate EVA copolymer and FDA compliantFeatures: Yields film with outstanding low temperature strength, excellent clarity, and good heat seal.Applications: Film extrusion: ice bags, liquid packaging, laminations, and heavy-duty packaging.FDA Notes: Conforms to FDA regulation 21 CFR 177.1350 under condition of use C through G described in Table 2 of 21 CFR 176.170Film properties based on 1.0 guage (25 µm) thickness; blow-up ratio 2:1.Information provided by Huntsman Corporation
Physical Properties Metric English Comments
Density 0.930 g/cc
0.0336 lb/in³
ASTM D1505
Thickness 25.4 microns
1.00 mil
Melt Flow 0.50 g/10 min
0.50 g/10 min
ASTM D1238
Mechanical Properties Metric English Comments
Hardness, Shore D 45
45
ASTM D2240
Tensile Strength, Ultimate 19.0 MPa
2760 psi
ASTM D638
Tensile Strength, Yield 8.00 MPa
1160 psi
ASTM D638
Film Elongation at Break, MD 390 %
390 %
ASTM D882
Film Elongation at Break, TD 490 %
490 %
ASTM D882
Elongation at Break 910 %
910 %
ASTM D638
Modulus of Elasticity 0.173 GPa
25.1 ksi
Secant; ASTM D638
Secant Modulus, MD 0.0950 GPa
13.8 ksi
ASTM D882
Secant Modulus, TD 0.115 GPa
16.7 ksi
ASTM D882
Dart Drop 14.0 g/micron
355 g/mil
ASTM D1709
Dart Drop Test 355 g
0.783 lb
ASTM D1709
Film Tensile Strength at Break, MD 25.0 MPa
3630 psi
ASTM D882
Film Tensile Strength at Break, TD 25.0 MPa
3630 psi
ASTM D882
Thermal Properties Metric English Comments
Vicat Softening Point 84.0 °C
183 °F
ASTM D1525
Optical Properties Metric English Comments
Haze 6.5 %
6.5 %
ASTM D1003
Gloss 63 %
63 %
at 45°; ASTM D523
Processing Properties Metric English Comments
Melt Temperature 199 - 210 °C
390 - 410 °F
Copyright © lookpolymers.com All Rights Reserved