Huntsman PE1065 Film Extrusion Polyethylene (discontinued **)
| Category | Polymer , Film , Thermoplastic , Polyethylene (PE) , LDPE , Low Density Polyethylene (LDPE), Film Grade |
| Manufacturer | |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Huntsman PE1065 Film Extrusion Polyethylene
(discontinued **).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Homopolymer and FDA compliant.Features: Yields film with excellent optical and machinability.Applications: Film extrusion: soft goods and other high clarity packaging.FDA Notes: Conforms to FDA regulation 21 CFR 177.1520 (c)2.2 under condition of use B through H described in Table 2 of 21 CFR 176.170Film properties based on 1.0 guage (25 µm) thickness; blow-up ratio 2:1.Information provided by Huntsman Corporation
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.924 g/cc | 0.0334 lb/in³ | ASTM D1505 |
| Thickness | 25.4 microns | 1.00 mil | |
| Melt Flow | 2.0 g/10 min | 2.0 g/10 min | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 55 | 55 | ASTM D2240 |
| Tensile Strength, Ultimate | 10.0 MPa | 1450 psi | ASTM D638 |
| Tensile Strength, Yield | 12.0 MPa | 1740 psi | ASTM D638 |
| Film Elongation at Break, MD | 315 % | 315 % | ASTM D882 |
| Film Elongation at Break, TD | 510 % | 510 % | ASTM D882 |
| Elongation at Break | 400 % | 400 % | ASTM D638 |
| Modulus of Elasticity | 0.297 GPa | 43.1 ksi | Secant; ASTM D638 |
| Secant Modulus, MD | 0.221 GPa | 32.1 ksi | ASTM D882 |
| Secant Modulus, TD | 0.262 GPa | 38.0 ksi | ASTM D882 |
| Dart Drop | 1.97 g/micron | 50.0 g/mil | ASTM D1709 |
| Dart Drop Test | 50.0 g | 0.110 lb | ASTM D1709 |
| Film Tensile Strength at Break, MD | 23.0 MPa | 3340 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 18.0 MPa | 2610 psi | ASTM D882 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Vicat Softening Point | 100 °C | 212 °F | ASTM D1525 |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Haze | 4.5 % | 4.5 % | ASTM D1003 |
| Gloss | 75 % | 75 % | at 45°; ASTM D523 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 163 - 174 °C | 325 - 345 °F |
Users viewing this material also viewed the following:
- Quadrant EPP Semitron® 420 ESd V (ASTM Product Data Sheet)
- BASF Capron® 5202CQ Blend HS Blend Nylon 66 (Conditioned) (discontinued **)
- Lubriplate L0751 Heat Transfer Oil Specialty Oil and Fluid
- Solvay Chemicals SOLVOKANE® E1.5
- Covestro Prism® CM-200 Polyurethane Solid RIM, MDI-based 2-Component Liquid System
- DuPont Performance Polymers Delrin® 570 NC000 Acetal (POM) (Unverified Data**)
- A. Schulman ComAlloy Hiloy® 443 Glass Reinforced, PET Alloy
- Addiplast Addinyl A2 Nylon 66
- ATI Allvac® 520 Nickel Superalloy, Heat Treatment: 1121°C (2050°F) + Age
- Haynes 230® alloy, GMAW deposit weld metal
Copyright © lookpolymers.com All Rights Reserved