Humiseal 1B12 Acrylic Conformal Coating
| Category | Polymer , Adhesive , Thermoset , Acrylic/Cyanoacrylate Adhesive |
| Manufacturer | Humiseal |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Humiseal 1B12 Acrylic Conformal Coating.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Humiseal 1B12 Acrylic Conformal CoatingHigh moisture resistanceExcellent dielectrical propertiesSelective chemical resistanceExcellent repairabilityPasses thermal shock test (MIL-I-46058C)Flammability (self extinguishing) (ASTM D635)Poor resistance to solvents (IPC CC 830)Recommended Stripper: 1080Recommended Thinner: 503/521 Cure Type: Room Temp or Heat
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.875 g/cc | 0.0316 lb/in³ | ASTM D1475 |
| Solids Content | 20 % | 20 % | Fed Std 141 Method 4044 |
| Volatile Organic Compounds (VOC) Content | 701 g/l | 701 g/l | |
| Viscosity | 40 cP | 40 cP | Fed Std Method 4287 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Modulus of Elasticity | 0.06744 GPa | 9.782 ksi |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 56.0 µm/m-°C @Temperature 20.0 °C |
31.1 µin/in-°F @Temperature 68.0 °F |
|
| Maximum Service Temperature, Air | 125 °C | 257 °F | |
| Minimum Service Temperature, Air | -65.0 °C | -85.0 °F | |
| Glass Transition Temp, Tg | 32.0 °C | 89.6 °F | |
| Flash Point | -1.11 °C | 30.0 °F | ASTM D56 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Surface Resistance | 3.00e+10 ohm | 3.00e+10 ohm | Moisture Resistance; MIL-I-46058C |
| Insulation Resistance | 2.50e+14 ohm | 2.50e+14 ohm | Insulation Resistance; MIL-I-46058C |
| Dielectric Constant | 2.8 | 2.8 | ASTM D1 50 65T |
| Dielectric Breakdown | >= 1500 V | >= 1500 V | Dielectric Withstand; MIL-I-46058C |
| Dissipation Factor | 0.010 | 0.010 | ASTM D1 50 65T |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Cure Time | 10.0 min | 0.167 hour | Dry Time to Handling; Fed Std 141 4061 |
| 30.0 min @Temperature 170 °C |
0.500 hour @Temperature 338 °F |
||
| >= 1440 min @Temperature 23.0 °C |
>= 24.0 hour @Temperature 73.4 °F |
||
| Shelf Life | 12.0 Month @Temperature 23.0 °C |
12.0 Month @Temperature 73.4 °F |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Coverage | 330 ft²/gal |
Users viewing this material also viewed the following:
- TSE Industries Millathane® CM Millable Polyether Urethane Rubber with 20 PHR N650 Filler
- Solvay RHEOZAN Biopolymer
- Chase Plastics CP Pryme® N330GL (COND, 50% RH) Nylon 6 (Utility Grade), 30% Glass Fiber Reinforced, Internally Lubricated
- United Cast Bar Unibar 700-2 Continuously Cast Spheroidal Graphite Iron
- Wellman EcoLon® MRGF1518-BK Mineral/Glass Fiber Reinforced Nylon 66, Lubricated, Heat Stabilized, PCR
- Eurostar Starpylen MZ006S PP, Glass Fiber Filled, Injection Molded
- DuPont Performance Polymers Zytel® 101L NC010 Nylon 66 (Unverified Data**)
- Ascend Performance Materials Vydyne® R633 Nylon 66 Copolymer, 33% Glass Filled, Conditioned (2.5% Moisture)
- Zircar Zirconia ZG Low Mass Zirconia Grog Insulation
Copyright © lookpolymers.com All Rights Reserved