Honeywell Capran® Oxyshield™ OEB (0.60 mil) Monoaxially Oriented, Co-Extruded Nylon 6/EVOH/Nylon 6 Clear Film

Category Polymer , Film , Thermoplastic , Nylon , Nylon 6 , Nylon 6, Film Grade
Manufacturer Honeywell
Trade Name Capran® Oxyshield™
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Honeywell Capran® Oxyshield™ OEB (0.60 mil) Monoaxially Oriented, Co-Extruded Nylon 6/EVOH/Nylon 6 Clear Film.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Description: Oxyshieldâ„¢ Oriented Extra Barrier is a 0.60 mil (15 micron) monoaxially oriented, co-extruded nylon 6/EVOH/nylon 6 clear film having excellent gas barrier through a broad range of relative humidity. The film provides high strength, good chemical resistance, and excellent flavor and aroma barrier for food packaging. Information provided by Honeywell.
Physical Properties Metric English Comments
Density 1.16 g/cc
0.0420 lb/in³
Yield Density
Water Vapor Transmission 140 g/m²/day
9.02 g/100 in²/day
100°F (37.8°C) / 100%RH; ASTM F1249
Oxygen Transmission Rate 0.230 cc/m²/day
0.0148 cc/100 in²/day
50°F (10°C) / 0%RH; ASTM D3985
0.620 cc/m²/day
0.0399 cc/100 in²/day
73°F (23°F) / 65%RH; ASTM D3985
0.930 cc/m²/day
0.0599 cc/100 in²/day
73°F (23°C) / 0%RH; ASTM D3985
Thickness 15.2 microns
0.600 mil
Surface Tension >= 56 dynes/cm
>= 56 dynes/cm
treated side; ASTM D2578
Mechanical Properties Metric English Comments
Film Tensile Strength at Yield, TD 68.9 - 82.7 MPa
10000 - 12000 psi
ASTM D882
Film Elongation at Break, MD 55 - 80 %
55 - 80 %
ASTM D882
Film Elongation at Break, TD 180 - 425 %
180 - 425 %
ASTM D882
Secant Modulus, MD 3.275 - 4.689 GPa
475.0 - 680.1 ksi
ASTM D882
Secant Modulus, TD 2.586 - 3.448 GPa
375.1 - 500.1 ksi
ASTM D882
Coefficient of Friction 0.25 - 0.57
0.25 - 0.57
film to stainless steel; ASTM D1894
0.66 - 2.0
0.66 - 2.0
film to film; ASTM D1894
Tear Strength Test 925 - 1450
925 - 1450
graves tear TD, grams/mil; ASTM D1004
1000 - 1400
1000 - 1400
graves tear MD, grams/mil; ASTM D1004
Film Tensile Strength at Break, MD 200 - 290 MPa
29000 - 42000 psi
ASTM D882
Film Tensile Strength at Break, TD 48.3 - 96.5 MPa
7000 - 14000 psi
ASTM D882
Thermal Properties Metric English Comments
Shrinkage, MD <= 11 %
<= 11 %
350°F / 177°C - 10 min.; ASTM D1204
Shrinkage, TD <= 2.5 %
<= 2.5 %
350°F / 177°C - 10 min.; ASTM D1204
Optical Properties Metric English Comments
Haze <= 5.0 %
<= 5.0 %
ASTM D1003
Transmission, Visible 90 %
90 %
clear; thickness not quantified