Honeywell Capran® Emblem™ MT1500 Bi-Axially Oriented Nylon 6 Film

Category Polymer , Film , Thermoplastic , Nylon , Nylon 6 , Nylon 6, Film Grade
Manufacturer Honeywell
Trade Name Capran® Emblem™
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Honeywell Capran® Emblem™ MT1500 Bi-Axially Oriented Nylon 6 Film.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Description: Capran® Emblem™ MT1500 is a 0.60 mil (15 micron) biaxially oriented nylon 6 film with a metallized barrier coating well suited for high barrier packaging applications. Information provided by Honeywell.
Physical Properties Metric English Comments
Density 1.16 g/cc
0.0420 lb/in³
Yield Density
Water Vapor Transmission 2.60 g/m²/day
0.167 g/100 in²/day
100°F / 100%RH); ASTM F1249
Oxygen Transmission Rate 1.10 cc/m²/day
0.0708 cc/100 in²/day
77°F / 0% / RH; ASTM D3985
Thickness 15.2 microns
0.600 mil
Surface Tension >= 50 dynes/cm
>= 50 dynes/cm
untreated side; ASTM D5946
Mechanical Properties Metric English Comments
Film Elongation at Break, MD 60 - 110 %
60 - 110 %
ASTM D882
Film Elongation at Break, TD 65 - 90 %
65 - 90 %
ASTM D882
Secant Modulus, MD 2.413 - 3.516 GPa
350.0 - 510.0 ksi
ASTM D882
Secant Modulus, TD 2.275 - 3.448 GPa
330.0 - 500.1 ksi
ASTM D882
Coefficient of Friction 0.18 - 0.27
0.18 - 0.27
film to stainless steel; ASTM D1894
0.59 - 0.90
0.59 - 0.90
film to film; ASTM D1894
Tear Strength Test 1100 - 1500
1100 - 1500
graves tear MD, grams/mil; ASTM D1004
1100 - 1500
1100 - 1500
graves tear TD, grams/mil; ASTM D1004
Film Tensile Strength at Break, MD 221 - 303 MPa
32000 - 44000 psi
ASTM D882
Film Tensile Strength at Break, TD 200 - 283 MPa
29000 - 41000 psi
ASTM D882
Thermal Properties Metric English Comments
Shrinkage, MD 1.4 - 2.4 %
1.4 - 2.4 %
320°F / 160°C - 5 minutes; ASTM D1204
Shrinkage, TD 0.20 - 0.70 %
0.20 - 0.70 %
320°F / 160°C - 5 minutes; ASTM D1204
Descriptive Properties Value Comments
Helium Transition Rate max 93 cc/m2/day
ASTM 1434