Honeywell Aegis™ HFX High Barrier Nylon  (discontinued **)

Category Polymer , Film , Thermoplastic , Nylon
Manufacturer
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Honeywell Aegis™ HFX High Barrier Nylon  (discontinued **).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Description: Aegis® HFX is an oxygen scavenging polyamide composition formulated specifically for use in high performance packaging applications where high gas barrier is required. This product is useful in injection and extrusion molding applications. Aegis® HFX offers high oxygen barrier, even at high humidity, outstanding delamination resistance and whitening resistance, clarity and easy processing (particularly in the PET co-injection stretch blow molding process).Information provided by Honeywell.
Physical Properties Metric English Comments
Specific Gravity 1.14 g/cc
1.14 g/cc
ASTM D1505
Bulk Density 0.730 g/cc
0.0264 lb/in³
ISO 60
Oxygen Transmission <= 0.000787 cc-mm/m²-24hr-atm
<= 0.00200 cc-mil/100 in²-24hr-atm
80% RH, 23°C, cast film
Melt Index of Compound 13 g/10 min

@Load 2.16 kg,
Temperature 260 °C
13 g/10 min

@Load 4.76 lb,
Temperature 500 °F
ISO 1133
26 g/10 min

@Load 2.16 kg,
Temperature 280 °C
26 g/10 min

@Load 4.76 lb,
Temperature 536 °F
ISO 1133
Mechanical Properties Metric English Comments
Tensile Strength at Break 51.4 MPa
7450 psi
ISO 527
Tensile Strength, Yield 83.4 MPa
12100 psi
ISO 527
Elongation at Break 192 %
192 %
ISO 527
Elongation at Yield 5.2 %
5.2 %
ISO 527
Flexural Strength 110 MPa
16000 psi
ISO 178
Flexural Modulus 2.54 GPa
368 ksi
ISO 178
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 72.5 °C
163 °F
ISO 1133
Deflection Temperature at 1.8 MPa (264 psi) 66.8 °C
152 °F
ISO 1133
Glass Transition Temp, Tg 82.0 °C
180 °F
DSC method
Processing Properties Metric English Comments
Processing Temperature 265 - 280 °C
509 - 536 °F
Manifold
Feed Temperature 35.0 °C
95.0 °F
Nozzle Temperature 265 °C
509 °F
Zone 1 245 °C
473 °F
Zone 2 265 °C
509 °F
Zone 3 265 °C
509 °F
Zone 4 265 °C
509 °F
Zone 5 265 °C
509 °F
Descriptive Properties Value Comments
Melt Temperature Amorphous
Oxygen Scav. Capacity min 10 cc/g
GC Method