Hippe SI GC 21 Woven Glass Cloth Reinforced Silicone Resin - Round, Rolled Tube

Category Polymer , Thermoset , Silicone , Silicone, Molded, Glass Fiber Filled
Manufacturer Erhard Hippe KG
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Hippe SI GC 21 Woven Glass Cloth Reinforced Silicone Resin - Round, Rolled Tube.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Good mechanical, electrical and electronic applications when exposed to high relative humidity.Information provided by Hippe.
Physical Properties Metric English Comments
Specific Gravity 1.60 - 1.80 g/cc
1.60 - 1.80 g/cc
IEC 1212-2 7.2
Mechanical Properties Metric English Comments
Flexural Strength >= 100 MPa

@Diameter >=100 mm
 >= 14500 psi

@Diameter >=3.94 in
 Perpendicular to laminations; IEC 1212-2 4.1
Compressive Strength >= 40.0 MPa
>= 5800 psi
Axial; IEC 1212-2 4.2
Electrical Properties Metric English Comments
Insulation Resistance >= 1.00e+8 ohm

@Diameter 8.00 - 10.0 mm
 >= 1.00e+8 ohm

@Diameter 0.315 - 0.394 in
 After immersion in water; IEC 1212-2 5.2
Dielectric Constant <= 5.0

@Frequency 1.00e+6 Hz
 <= 5.0

@Frequency 1.00e+6 Hz
 IEC 1212-2 5.3
Dielectric Breakdown >= 35000 V

@Temperature 90.0 °C,
Time 20.0 sec
 >= 35000 V

@Temperature 194 °F,
Time 0.00556 hour
 Step -by-step test, In oil, parallel to laminations; IEC 1212-2 5.1
>= 35000 V

@Temperature 90.0 °C,
Time 60.0 sec
 >= 35000 V

@Temperature 194 °F,
Time 0.0167 hour
 Proof test, In oil, parallel to laminations; IEC 1212-2 5.1
Dissipation Factor <= 0.010

@Frequency 1.00e+6 Hz
 <= 0.010

@Frequency 1.00e+6 Hz
 IEC 1212-2 5.3
<= 0.050

@Frequency 48.0 - 62.0 Hz
 <= 0.050

@Frequency 48.0 - 62.0 Hz
 IEC 1212-2 5.3
Descriptive Properties Value Comments
Cohesion between layers > 50 MPa
IEC 1212-2 4.3, Internal diameter <100 mm
Thermal Endurance 180 T.I.
IEC 1212-2 7.1
Water Absorption < 1 mg/cm²
IEC 1212-2 7.1