Hippe PA 66 GF 30 Nylon 66 30% Glass fiber Reinforced
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 30% Glass Fiber Filled |
| Manufacturer | Erhard Hippe KG |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Hippe PA 66 GF 30 Nylon 66 30% Glass fiber Reinforced.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
These polyamide components being reinforced with glass fiber up to 30% are not only highly wear-resistant, but also show high mechanical strength, stiffness and dimensional stability. They can also be used under high working temperatures.Information provided by Hippe.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.37 g/cc | 1.37 g/cc | DIN 53 479 |
| Moisture Absorption at Equilibrium | 1.5 % | 1.5 % | Absorption of humidity in standard operating environment; DIN 53 715 |
| Water Absorption at Saturation | 5.5 % | 5.5 % | DIN 53 495 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Ball Indentation Hardness | 200 - 270 MPa @Time 30.0 sec |
29000 - 39200 psi @Time 0.00833 hour |
DIN 53 456 |
| Elongation at Break | 3.5 % | 3.5 % | dry; DIN 53 455 |
| 5.0 % | 5.0 % | cond.; DIN 53 455 | |
| Tensile Modulus | 7.50 GPa | 1090 ksi | cond.; DIN 53 457 |
| 9.70 GPa | 1410 ksi | dry; DIN 53 457 | |
| Charpy Impact, Notched | 1.30 - 1.70 J/cm² | 6.19 - 8.09 ft-lb/in² | DIN 53 453 |
| Coefficient of Friction, Dynamic | 0.45 - 0.50 | 0.45 - 0.50 | Against steel, p=0.05 N/mm², v=0.6 m/s, hardened and ground |
| Tear Strength Test | 140 | 140 | in MPa; Cond.; DIN 53 455 |
| 200 | 200 | in MPa; dry; DIN 53 455 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 20.0 - 30.0 µm/m-°C | 11.1 - 16.7 µin/in-°F | |
| Specific Heat Capacity | 1.50 J/g-°C | 0.359 BTU/lb-°F | |
| Thermal Conductivity | 0.270 W/m-K | 1.87 BTU-in/hr-ft²-°F | |
| Melting Point | 255 °C | 491 °F | DIN 53 736 |
| Maximum Service Temperature, Air | 110 °C | 230 °F | Continuous use |
| 200 °C | 392 °F | Short Periods | |
| Deflection Temperature at 0.46 MPa (66 psi) | 250 °C | 482 °F | ISO-R 75 Method B |
| Deflection Temperature at 1.8 MPa (264 psi) | 250 °C | 482 °F | ISO-R 75 Method A |
| Glass Transition Temp, Tg | 5.00 °C | 41.0 °F | cond., dynamic; DIN 53 736 |
| 50.0 °C | 122 °F | dry, dynamic; DIN 53 736 | |
| Flammability, UL94 | HB | HB |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Color | black | |
| Creep Resistance | Grade CTI 475 | DIN 53 480, IEC-112, VDE 0303 Part 1 |
| Resistance to hot water, suds | resistant in some conditions |