Hexcel® Redux® 870 A/B Two Component Shimming and Potting Epoxy Paste Adhesive

Category	Polymer , Adhesive , Thermoset , Epoxy , Epoxy Adhesive
Manufacturer	Hexcel
Trade Name
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Hexcel® Redux® 870 A/B Two Component Shimming and Potting Epoxy Paste Adhesive.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Redux 870 A/B is a two component high performance epoxy paste adhesive, ideal for use as a Liquid Shim or for potting applications. This high temperature performing thixotropic adhesive has been specially formulated for bonding of fibre-reinforced composite and metal substrates.Features: Thixotropic, gap filling high performance liquid shim adhesive; Easy 2:1 volume mix ratio - available in dual-cartridges with static mixers; Room temperature curing; Long working life at ambient temperatures; Excellent compression and shear properties; High temperature performance.

Physical Properties	Metric	English	Comments
Specific Gravity	1.10 g/cc	1.10 g/cc	Redux 870 B
	1.16 g/cc	1.16 g/cc	Mixed Adhesive
	1.20 g/cc	1.20 g/cc	Redux 870 A

Mechanical Properties	Metric	English	Comments
Compressive Yield Strength	98.0 MPa @Temperature 23.0 °C	14200 psi @Temperature 73.4 °F	Cured 5 days at 23°C; ISO 604
Shear Strength	11.0 MPa @Temperature 150 °C	1600 psi @Temperature 302 °F	Lap Shear; Cured 5 days at 23°C; Substrate: 2024 T3 Aluminum Alloy (CSA pretreated, Unprimed); EN2243-1
	22.0 MPa @Temperature 120 °C	3190 psi @Temperature 248 °F	Lap Shear; Cured 5 days at 23°C; Substrate: 2024 T3 Aluminum Alloy (CSA pretreated, Unprimed); EN2243-1
	27.0 MPa @Temperature 80.0 °C	3920 psi @Temperature 176 °F	Lap Shear; Cured 5 days at 23°C; Substrate: 2024 T3 Aluminum Alloy (CSA pretreated, Unprimed); EN2243-1
	43.0 MPa @Temperature 23.0 °C	6240 psi @Temperature 73.4 °F	Lap Shear; Cured 5 days at 23°C; Substrate: 2024 T3 Aluminum Alloy; EN2243-1

Descriptive Properties	Value	Comments
Color	Mixed Adhesive: Grey
	Redux 870 A: Dark Grey
	Redux 870 B: Off White