Hexcel® Redux® 610W (0.06 psf) Flame retarded epoxy film adhesive

Category	Polymer , Adhesive , Film , Thermoset , Epoxy , Epoxy Adhesive
Manufacturer	Hexcel
Trade Name
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Hexcel® Redux® 610W (0.06 psf) Flame retarded epoxy film adhesive.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Redux 610 is a modified, flame-retarded epoxy film adhesive curing at 250°F. It is suitable for bonding metal to metal and for sandwich structures where flame retardancy and low heat release are required. Redux 610 is a hot melt film which is free from solvents and consequently has a very low volatile content.Features: Cures in 1 hour at 250°F; Good lap-shear performance up to 212°F; Good peel performance in sandwich structures up to 175°F; Meets the heat release requirements of IMO test MSC 61 (67); Good tack, drape and handleability; Very low volatile content and low out gassing properties; Available unsupported or with a very lightweight glass carrier.Applications: Metal to metal bonding; Sandwich constructions; Flame retarded performance

Physical Properties	Metric	English	Comments
Storage Temperature	-17.8 °C	0.000 °F

Mechanical Properties	Metric	English	Comments
Shear Strength	13.00 MPa @Temperature 100 °C	1885 psi @Temperature 212 °F	Lap Shear
	19.00 MPa @Temperature 80.0 °C	2755 psi @Temperature 176 °F	Lap Shear
	24.0 MPa @Temperature 50.0 °C	3480 psi @Temperature 122 °F	Lap Shear
	30.0 MPa @Temperature 22.2 °C	4350 psi @Temperature 72.0 °F	Lap Shear
Peel Strength	4.12 kN/m @Temperature 22.2 °C	23.5 pli @Temperature 72.0 °F	Floating Roller Peel

Processing Properties	Metric	English	Comments
Shelf Life	18.0 Month @Temperature -17.8 °C	18.0 Month @Temperature 0.000 °F

Descriptive Properties	Value	Comments
Areal Weight (psf)	0.06
Climbing Drum Peel (in-lb/3in)	53.8	72°F
	78.5	176°F
Roll Width (in)	49
Standard Roll (ft2)	1075
Support	Woven Glass