Hexcel® HexWeb® HRH-10 - 1/8- 6.0 Aramid Fiber/Phenolic Resin Honeycomb

Category Other Engineering Material , Composite Core Material , Polymer , Thermoset , Aramid , Phenolic
Manufacturer Hexcel
Trade Name HexWeb®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Hexcel® HexWeb® HRH-10 - 1/8- 6.0 Aramid Fiber/Phenolic Resin Honeycomb.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Designation: Material-Cell Size-Density.Hexweb HRH-10 is manufactured from NOMEX aramid fiber sheets. A thermosetting adhesive is used to bond these sheets at the nodes, and after expanding to the hexagonal or OX-Core confiation, the block is dipped in phenolic resin. After curing the resin, slices are cut to the desired thickness. For special applications, such as air directionalizing, HexWeb HRH-10 can be provided without the phenolic resin. Using this process, a wide range of cell sizes, paper thicknesses, and densities can be produced.Information provided by HexCel
Physical Properties Metric English Comments
Density 0.0961 g/cc
0.00347 lb/in³
Mechanical Properties Metric English Comments
Compressive Yield Strength >= 5.86 MPa
>= 850 psi
Bare, min
>= 6.38 MPa
>= 925 psi
Stabilized, min
7.24 MPa
1050 psi
Bare, typ
7.757 MPa
1125 psi
Stabilized, typ
Compressive Modulus 0.414 GPa
60.0 ksi
Stabilized, typ
Shear Modulus 0.0448 GPa
6.50 ksi
Plate Shear, W Direction, typ
0.0896 GPa
13.0 ksi
Plate Shear, L Direction, typ
Shear Strength >= 1.17 MPa
>= 170 psi
Plate Shear, W Direction, min
1.38 MPa
200 psi
Plate Shear, W Direction, typ
>= 2.28 MPa
>= 330 psi
Plate Shear, L Direction, min
2.65 MPa
385 psi
Plate Shear, L Direction, typ