Hexcel® HexWeb® CR-PAA™ 3/8-5056-0.001 Phosphoric Acid Anodized Aluminum Honeycomb

Category Metal , Metal Foam, Mesh, or Honeycomb , Nonferrous Metal , Aluminum Alloy , 5000 Series Aluminum Alloy
Manufacturer Hexcel
Trade Name HexWeb®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Hexcel® HexWeb® CR-PAA™ 3/8-5056-0.001 Phosphoric Acid Anodized Aluminum Honeycomb.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Grade is designated as "Cell Size-Alloy-Foil Gauge." The life cycle of aluminum honeycomb sandwich structures in a given application can be directly related to the quality of the bond between the face sheets that carry bending loads and the honeycomb that carries the shear loads. The adhesive is the interface between the facing and the core in the same way that the oxide on the aluminum and the primer that has been applied to it is the interface between the honeycomb substrate material and the bonding adhesive. This interface is critical to the performance of honeycomb bonded assemblies.Information provided by HexCel
Physical Properties Metric English Comments
Density 0.0256 g/cc
0.000926 lb/in³
Nominal
Mechanical Properties Metric English Comments
Compressive Yield Strength >= 0.517 MPa
>= 75.0 psi
Bare, min
>= 0.552 MPa
>= 80.0 psi
Stabilized, min
0.689 MPa
100 psi
Bare, typ
0.758 MPa
110 psi
Stabilized, typ
Compressive Modulus 0.207 GPa
30.0 ksi
Stabilized, typ
Shear Modulus 0.0724 GPa
10.5 ksi
Plate Shear, W Direction, typ
0.138 GPa
20.0 ksi
Plate Shear, L Direction, typ
Shear Strength >= 0.262 MPa
>= 38.0 psi
Plate Shear, W Direction, min
0.414 MPa
60.0 psi
Plate Shear, W Direction, typ
>= 0.538 MPa
>= 78.0 psi
Plate Shear, L Direction, min
0.621 MPa
90.0 psi
Plate Shear, L Direction, typ