Hexcel® HexTow™ AS4 Carbon Fiber

Category Carbon , Carbon Fiber
Manufacturer Hexcel
Trade Name HexTow™
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Hexcel® HexTow™ AS4 Carbon Fiber.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
HexTow™ AS4 carbon fiber is a continuous, high strength, high strain, PAN based fiber available in 3,000 (3K), 6,000 (6K), and 12,000 (12K) filament count tows. The fiber has been surface treated and can be sized to improve its interlaminar shear properties, handling characteristics, and structural properties, and is suggested for use in weaving, prepregging, filament winding, pultrusion, and molding compounds. Sizing compatible with various resin systems are available to improve handling characteristics and structural properties.Information provided by Hexcel
Physical Properties Metric English Comments
Density 1.79 g/cc
0.0647 lb/in³
Filament Diameter 7.1 µm
7.1 µm
Mechanical Properties Metric English Comments
Tensile Strength, Yield 2221 MPa
322100 psi
Typical epoxy composite property
4480 MPa
650000 psi
Typical fiber property
Elongation at Break 1.8 %
1.8 %
Calculated from tow test data
Tensile Modulus 141 GPa
20500 ksi
Typical epoxy composite property
231 GPa
33500 ksi
Typical fiber property; Chord 6000-1000
Flexural Modulus 128 GPa
18600 ksi
Typical epoxy composite property
Shear Strength 124 MPa
18000 psi
Typical epoxy composite property; short-beam
Component Elements Properties Metric English Comments
Carbon, C 94 %
94 %
Electrical Properties Metric English Comments
Volume Resistivity 0.32 ohm-cm
0.32 ohm-cm
12K
Surface Resistance 0.00153 ohm
0.00153 ohm
12K
Descriptive Properties Value Comments
Approximate Yield (m/g) 1.17
12K
2.34
6K
4.76
3K
Fiber Volume (%) 62
Filament Shape Round
Tow Cross-Sectional Area (mm2) 0.12
3K
0.24
6K
0.48
12K
Twist None
Weight/Length (g/m) 0.21
3K
0.427
6K
0.858
12K