Hexcel® HexPly® M36/NC2 180°C (350°F) Curing Epoxy Matrix, Multiaxial Fabric Laminate (NC2)

Category Polymer , Thermoset , Epoxy , Epoxy Cure Resin
Manufacturer Hexcel
Trade Name HexPly®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Hexcel® HexPly® M36/NC2 180°C (350°F) Curing Epoxy Matrix, Multiaxial Fabric Laminate (NC2).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Uses Hexcel NC2 non-crimp fabric based on Tenax HTS fiber; Quasi-isotropic lay-up based on 1072 gsm quadaxial NC2 fabric (267 gsm/ply); Laminates manufactured via resin film infusionInformation provided by HexCel
Mechanical Properties Metric English Comments
Tensile Strength, Yield 432 MPa

@Temperature 23.0 °C
62700 psi

@Temperature 73.4 °F
Open Hole TS
568 MPa

@Temperature 23.0 °C
82400 psi

@Temperature 73.4 °F
Tensile Modulus 52.0 GPa

@Temperature 23.0 °C
7540 ksi

@Temperature 73.4 °F
Compressive Yield Strength 225 MPa
32600 psi
Compression strength after impact, 30J
270 MPa
39200 psi
Compression strength after impact, 20J
291 MPa
42200 psi
Compression strength after impact, 6J
474 MPa

@Temperature 23.0 °C
68700 psi

@Temperature 73.4 °F
Open Hole
587 MPa

@Temperature 23.0 °C
85100 psi

@Temperature 73.4 °F
Shear Strength 39.0 MPa

@Temperature 100 °C
5660 psi

@Temperature 212 °F
Interlaminar shear
45.0 MPa

@Temperature 23.0 °C
6530 psi

@Temperature 73.4 °F
Interlaminar shear