Hexcel® HexPly® M12 135°C Curing Epoxy Matrix, 45% 46280 Fiber

Category Polymer , Thermoset , Epoxy , Epoxy Cure Resin
Manufacturer Hexcel
Trade Name HexPly®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Hexcel® HexPly® M12 135°C Curing Epoxy Matrix, 45% 46280 Fiber.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Information provided by HexCel
Physical Properties Metric English Comments
Density 1.24 g/cc
0.0448 lb/in³
Resin Density
1.75 g/cc
0.0632 lb/in³
Fibre Density
Mechanical Properties Metric English Comments
Tensile Strength, Yield 550 MPa
79800 psi
RT; Dry; EN2561
650 MPa
94300 psi
90º, RT, Dry; EN2561
600 MPa

@Temperature 75.0 °C
87000 psi

@Temperature 167 °F
90º, Wet; EN2561
600 MPa

@Temperature 100 °C
87000 psi

@Temperature 212 °F
90º, Wet; EN2561
650 MPa

@Temperature 75.0 °C
94300 psi

@Temperature 167 °F
Wet; EN2561
700 MPa

@Temperature 100 °C
102000 psi

@Temperature 212 °F
Wet; EN2561
Tensile Modulus 57.0 GPa
8270 ksi
90º, RT, Dry; EN2561
65.0 GPa
9430 ksi
RT; Dry; EN2561
60.0 GPa

@Temperature 75.0 °C
8700 ksi

@Temperature 167 °F
90º, Wet; EN2561
62.0 GPa

@Temperature 100 °C
8990 ksi

@Temperature 212 °F
Wet; EN2561
63.0 GPa

@Temperature 100 °C
9140 ksi

@Temperature 212 °F
90º, Wet; EN2561
66.0 GPa

@Temperature 75.0 °C
9570 ksi

@Temperature 167 °F
Wet; EN2561
Compressive Yield Strength 650 MPa
94300 psi
RT; Dry; DIN65380
730 MPa
106000 psi
90º, RT, Dry; DIN65380
415 MPa

@Temperature 100 °C
60200 psi

@Temperature 212 °F
Wet; DIN65380
435 MPa

@Temperature 100 °C
63100 psi

@Temperature 212 °F
90º, Wet; DIN65380
495 MPa

@Temperature 75.0 °C
71800 psi

@Temperature 167 °F
90º, Wet; DIN65380
500 MPa

@Temperature 75.0 °C
72500 psi

@Temperature 167 °F
Wet; DIN65380
Compressive Modulus 57.0 GPa
8270 ksi
RT; Dry; DIN65380
61.0 GPa
8850 ksi
90º, RT, Dry; DIN65380
50.0 GPa

@Temperature 100 °C
7250 ksi

@Temperature 212 °F
90º, Wet; DIN65380
52.0 GPa

@Temperature 100 °C
7540 ksi

@Temperature 212 °F
Wet; DIN65380
53.0 GPa

@Temperature 75.0 °C
7690 ksi

@Temperature 167 °F
Wet; DIN65380
60.0 GPa

@Temperature 75.0 °C
8700 ksi

@Temperature 167 °F
90º, Wet; DIN65380
Shear Strength 60.0 MPa
8700 psi
0º, ILSS (Short Beam), RT, Dry; EN2563
75.0 MPa
10900 psi
In-Plane, RT, Dry; EN6031
35.0 MPa

@Temperature 100 °C
5080 psi

@Temperature 212 °F
0º, ILSS (Short Beam), Wet; EN2563
42.0 MPa

@Temperature 75.0 °C
6090 psi

@Temperature 167 °F
0º, ILSS (Short Beam), Wet; EN2563
58.0 MPa

@Temperature 100 °C
8410 psi

@Temperature 212 °F
In-Plane, Wet; EN6031
68.0 MPa

@Temperature 75.0 °C
9860 psi

@Temperature 167 °F
In-Plane, Wet; EN6031
Processing Properties Metric English Comments
Shelf Life 14.0 Month

@Temperature -18.0 °C
14.0 Month

@Temperature -0.400 °F
Descriptive Properties Value Comments
Cured Thickness per Ply (cm) 0.38
Fiber Volume (%) 50