Hexcel® HexPly® F593 Epoxy Resin, T2G190 Carbon Tape

Category Polymer , Thermoset , Carbon Fiber/Thermoset Composite , Epoxy , Epoxy/Carbon Fiber Composite
Manufacturer Hexcel
Trade Name HexPly®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Hexcel® HexPly® F593 Epoxy Resin, T2G190 Carbon Tape.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Hexcel designation: T2GXXX-12"-F593; Fiber: Amoco T-300/12kInformation provided by HexCel
Physical Properties Metric English Comments
Volatiles 1.0 - 4.0 %
1.0 - 4.0 %
Prepreg
Mechanical Properties Metric English Comments
Tensile Strength, Yield 3.372 MPa

@Temperature 93.0 °C
 489.1 psi

@Temperature 199 °F
 Sandwich Flatwise Tension, Dry
5.192 MPa

@Temperature 24.0 °C
 753.0 psi

@Temperature 75.2 °F
 Sandwich Flatwise Tension, Dry
1269 MPa

@Temperature -54.0 °C
 184100 psi

@Temperature -65.2 °F
 Dry
1331 MPa

@Temperature 24.0 °C
 193000 psi

@Temperature 75.2 °F
 Dry
1427 MPa

@Temperature 71.0 °C
 207000 psi

@Temperature 160 °F
 Dry
1751 MPa

@Temperature 93.0 °C
 254000 psi

@Temperature 199 °F
 Dry
Tensile Modulus 120 GPa

@Temperature 24.0 °C
 17400 ksi

@Temperature 75.2 °F
 Dry
121.4 GPa

@Temperature 71.0 °C
 17610 ksi

@Temperature 160 °F
 Dry
123.4 GPa

@Temperature -54.0 °C
 17900 ksi

@Temperature -65.2 °F
 Dry
126.2 GPa

@Temperature 93.0 °C
 18300 ksi

@Temperature 199 °F
 Dry
Compressive Yield Strength 183 MPa

@Temperature 24.0 °C
 26500 psi

@Temperature 75.2 °F
 Compression After Impact, Dry
1234 MPa

@Temperature 71.0 °C
 179000 psi

@Temperature 160 °F
 Wet
1455 MPa

@Temperature 93.0 °C
 211000 psi

@Temperature 199 °F
 Dry
1538 MPa

@Temperature 71.0 °C
 223100 psi

@Temperature 160 °F
 Dry
1655 MPa

@Temperature 24.0 °C
 240000 psi

@Temperature 75.2 °F
 Dry
1786 MPa

@Temperature -59.0 °C
 259000 psi

@Temperature -74.2 °F
 Dry
Compressive Modulus 108.3 GPa

@Temperature -59.0 °C
 15710 ksi

@Temperature -74.2 °F
 Dry
113.8 GPa

@Temperature 93.0 °C
 16510 ksi

@Temperature 199 °F
 Dry
114.5 GPa

@Temperature 24.0 °C
 16610 ksi

@Temperature 75.2 °F
 Dry
115.1 GPa

@Temperature 71.0 °C
 16690 ksi

@Temperature 160 °F
 Dry
Descriptive Properties Value Comments
Cured Thickness per Ply (cm) 0.02-0.021
Laminate
Dry Resin Content (%) 36-40
Prepreg
Fiber Volume (%) 50-55
Laminate
Flow (%) 13-25