Hexcel® HexPly® F522 Epoxy Resin, F3C433 Carbon Fabric

Category Polymer , Thermoset , Carbon Fiber/Thermoset Composite , Epoxy , Epoxy/Carbon Fiber Composite
Manufacturer Hexcel
Trade Name HexPly®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Hexcel® HexPly® F522 Epoxy Resin, F3C433 Carbon Fabric.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Hexcel designation: F3C433-42"-F522; Fiber: Toho® G30/500-3KInformation provided by HexCel
Mechanical Properties Metric English Comments
Tensile Strength, Yield 903 MPa

@Temperature 24.0 °C
131000 psi

@Temperature 75.2 °F
Dry
Tensile Modulus 69.6 GPa

@Temperature 24.0 °C
10100 ksi

@Temperature 75.2 °F
Dry
Compressive Yield Strength 475 MPa

@Temperature 71.0 °C
68900 psi

@Temperature 160 °F
Wet (14 ± 1/2 days of water immersion at 160 ± 5°F (71 ± 3°C)
655 MPa

@Temperature 24.0 °C
95000 psi

@Temperature 75.2 °F
Dry
Shear Strength 26.2 MPa

@Temperature 71.0 °C
3800 psi

@Temperature 160 °F
Short Beam, Wet (14 ± 1/2 days of water immersion at 160 ± 5°F (71 ± 3°C)
64.8 MPa

@Temperature 24.0 °C
9400 psi

@Temperature 75.2 °F
Short Beam, Dry
Descriptive Properties Value Comments
Dry Resin Content (%) 37-41
Prepreg
Fiber Volume (%) 0.028
Laminate
Flow (%) 11-23
Wet Resin Content (%) 52
Laminate