- Hexcel® HexPly® F263 Epoxy Resin, W3T282 Carbon Fabric
Hexcel® HexPly® F263 Epoxy Resin, W3T282 Carbon Fabric
| Category | Polymer , Thermoset , Carbon Fiber/Thermoset Composite , Epoxy , Epoxy/Carbon Fiber Composite |
| Manufacturer | Hexcel |
| Trade Name | HexPly® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Hexcel® HexPly® F263 Epoxy Resin, W3T282 Carbon Fabric.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Hexcel designation: W3T282-42"-F263; Fiber: T300 CelionInformation provided by HexCel
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 541 MPa @Temperature 177 °C |
78500 psi @Temperature 351 °F |
|
| 570 MPa @Temperature 24.0 °C |
82700 psi @Temperature 75.2 °F |
||
| Tensile Modulus | 57.7 GPa @Temperature 177 °C |
8370 ksi @Temperature 351 °F |
|
| 60.7 GPa @Temperature 24.0 °C |
8800 ksi @Temperature 75.2 °F |
||
| Compressive Yield Strength | 575 MPa @Temperature 71.0 °C |
83400 psi @Temperature 160 °F |
|
| 648 MPa @Temperature 24.0 °C |
94000 psi @Temperature 75.2 °F |
||
| Shear Strength | 46.0 MPa @Temperature 177 °C |
6670 psi @Temperature 351 °F |
Short Beam |
| 56.0 MPa @Temperature 132 °C |
8120 psi @Temperature 270 °F |
Short Beam | |
| 72.0 MPa @Temperature -54.0 °C |
10400 psi @Temperature -65.2 °F |
Short Beam | |
| 74.0 MPa @Temperature 24.0 °C |
10700 psi @Temperature 75.2 °F |
Short Beam |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Cured Thickness per Ply (cm) | 0.018 | Laminate |
| Dry Resin Content (%) | 38-42 | Prepreg |
| Fiber Volume (%) | 61 | Laminate |
| Flow (%) | 9-22 |