Hexcel® HexPly® F263 Epoxy Resin, F3T584 Carbon Fabric

Category Polymer , Thermoset , Carbon Fiber/Thermoset Composite , Epoxy , Epoxy/Carbon Fiber Composite
Manufacturer Hexcel
Trade Name HexPly®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Hexcel® HexPly® F263 Epoxy Resin, F3T584 Carbon Fabric.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Hexcel designation: F3T584-42"-F263; Fiber: T300 CelionInformation provided by HexCel
Mechanical Properties Metric English Comments
Tensile Strength, Yield 579 MPa

@Temperature 177 °C
 84000 psi

@Temperature 351 °F
610 MPa

@Temperature 24.0 °C
 88500 psi

@Temperature 75.2 °F
Tensile Modulus 60.5 GPa

@Temperature 177 °C
 8770 ksi

@Temperature 351 °F
63.7 GPa

@Temperature 24.0 °C
 9240 ksi

@Temperature 75.2 °F
Compressive Yield Strength 585 MPa

@Temperature 71.0 °C
 84800 psi

@Temperature 160 °F
666 MPa

@Temperature 24.0 °C
 96600 psi

@Temperature 75.2 °F
Shear Strength 47.0 MPa

@Temperature 177 °C
 6820 psi

@Temperature 351 °F
 Short Beam
48.0 MPa

@Temperature 132 °C
 6960 psi

@Temperature 270 °F
 Short Beam
65.0 MPa

@Temperature -54.0 °C
 9430 psi

@Temperature -65.2 °F
 Short Beam
72.0 MPa

@Temperature 24.0 °C
 10400 psi

@Temperature 75.2 °F
 Short Beam
Descriptive Properties Value Comments
Cured Thickness per Ply (cm) 0.034
Laminate
Dry Resin Content (%) 35-39
Prepreg
Fiber Volume (%) 62
Laminate
Flow (%) 9-22