Hexcel® HexPly® ES 84 120°C Curing Epoxy Matrix, E-glass Balanced fabric 390 g/m2
| Category | Polymer , Thermoset , Epoxy , Epoxy/Glass SMC |
| Manufacturer | Hexcel |
| Trade Name | HexPly® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Hexcel® HexPly® ES 84 120°C Curing Epoxy Matrix, E-glass Balanced fabric 390 g/m2.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by HexCel
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 600 MPa | 87000 psi | 0° |
| Tensile Modulus | 21.0 GPa | 3050 ksi | 0° |
| Flexural Yield Strength | 700 MPa | 102000 psi | 0° |
| Flexural Modulus | 20.0 GPa | 2900 ksi | 0° |
| Compressive Yield Strength | 540 MPa | 78300 psi | 0° |
| Shear Strength | 60.0 MPa | 8700 psi | 0°, Short Beam |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Shelf Life | 14.0 Month @Temperature -18.0 °C |
14.0 Month @Temperature -0.400 °F |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Fiber Volume (%) | 50 | |
| Tack Life (days) | 30 |
Users viewing this material also viewed the following:
- Multibase Multi-Flex® TPE D 4701 GREY
- RheTech Products HP522-286 15% Talc Reinforced High Performance Polypropylene Copolymer, UV Stabilized, ZUCA Medium Graphite
- Polykemi AB POLYfill PPH K5040 Polypropylene Homopolymer, Mineral Reinforced
- SABIC Innovative Plastics Lexan® 3412HF PC
- Michelman® Resisto Coat™ PLUS Abrasion resistance coating
- Lucas-Milhaupt BRAZE 450 Silver Based Cadmium Free Filler Metal
- Multibase Multi-Flex® TPE A 6221 BLK
- Saint-Gobain Micaver® Glass-Mica Electrical Insulator, Transfer Moldings
- A. Schulman PAPERMATCH® H-3818 Specialty Masterbatch
- 3M Scotchcal™ ElectroCut™ 7125-86 Graphic Film
Copyright © lookpolymers.com All Rights Reserved