Hexcel® HexPly® 8552 Epoxy Matrix, SGP370-8H Fiber

Category Polymer , Thermoset , Epoxy , Epoxy Cure Resin
Manufacturer Hexcel
Trade Name HexPly®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Hexcel® HexPly® 8552 Epoxy Matrix, SGP370-8H Fiber.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Information provided by HexCel
Mechanical Properties Metric English Comments
Tensile Strength, Yield 402 MPa

@Temperature 25.0 °C
 58300 psi

@Temperature 77.0 °F
 Open Hole Tensile, Dry
896 MPa

@Temperature 104 °C
 130000 psi

@Temperature 220 °F
 90°, Dry
903 MPa

@Temperature -55.0 °C
 131000 psi

@Temperature -67.0 °F
 90°, Dry
958 MPa

@Temperature 25.0 °C
 139000 psi

@Temperature 77.0 °F
 90°, Dry
965 MPa

@Temperature -55.0 °C
 140000 psi

@Temperature -67.0 °F
 0°, Dry
1010 MPa

@Temperature 25.0 °C
 147000 psi

@Temperature 77.0 °F
 0°, Dry
Tensile Modulus 79.3 GPa

@Temperature 220 °C
 11500 ksi

@Temperature 428 °F
 90°, Dry
80.7 GPa

@Temperature -67.0 °C
 11700 ksi

@Temperature -88.6 °F
 90°, Dry
80.7 GPa

@Temperature 77.0 °C
 11700 ksi

@Temperature 171 °F
 90°, Dry
85.5 GPa

@Temperature 77.0 °C
 12400 ksi

@Temperature 171 °F
 0°, Dry
86.2 GPa

@Temperature -67.0 °C
 12500 ksi

@Temperature -88.6 °F
 0°, Dry
Flexural Yield Strength 1130 MPa

@Temperature 25.0 °C
 164000 psi

@Temperature 77.0 °F
 0°, Dry
Flexural Modulus 74.5 GPa

@Temperature 25.0 °C
 10800 ksi

@Temperature 77.0 °F
 0°, Dry
Compressive Yield Strength 276 MPa

@Temperature 25.0 °C
 40000 psi

@Temperature 77.0 °F
 Compression After Impact, Dry
339 MPa

@Temperature 25.6 °C
 49200 psi

@Temperature 78.0 °F
 Open Hole Compression, Dry
607 MPa

@Temperature 82.2 °C
 88000 psi

@Temperature 180 °F
 0°, Wet, Fill Compression
648 MPa

@Temperature 25.0 °C
 94000 psi

@Temperature 77.0 °F
 0°, Wet, Fill Compression
662 MPa

@Temperature 104 °C
 96000 psi

@Temperature 220 °F
 0°, Dry, Fill Compression
834 MPa

@Temperature 25.0 °C
 121000 psi

@Temperature 77.0 °F
 0°, Dry, Fill Compression
910 MPa

@Temperature -55.0 °C
 132000 psi

@Temperature -67.0 °F
 0°, Dry, Fill Compression
Shear Strength 62.7 MPa

@Temperature 82.2 °C
 9100 psi

@Temperature 180 °F
 0° Short Beam, Wet
74.5 MPa

@Temperature 104 °C
 10800 psi

@Temperature 220 °F
 0° Short Beam, Dry
83.4 MPa

@Temperature 25.0 °C
 12100 psi

@Temperature 77.0 °F
 0° Short Beam, Wet
89.6 MPa

@Temperature 25.0 °C
 13000 psi

@Temperature 77.0 °F
 0° Short Beam, Dry
90.3 MPa

@Temperature 104 °C
 13100 psi

@Temperature 220 °F
 +/- 45° In-Plane, Dry
101 MPa

@Temperature 25.0 °C
 14600 psi

@Temperature 77.0 °F
 +/- 45° In-Plane, Dry
Thermal Properties Metric English Comments
Maximum Service Temperature, Air 121 °C
250 °F
Epoxy Matrix Limit