Hexcel® HexPly® 8552 Epoxy Matrix, AS4 Fiber

Category Polymer , Thermoset , Epoxy , Epoxy Cure Resin
Manufacturer Hexcel
Trade Name HexPly®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Hexcel® HexPly® 8552 Epoxy Matrix, AS4 Fiber.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Information provided by HexCel
Mechanical Properties Metric English Comments
Tensile Strength, Yield 75.2 MPa

@Temperature 93.3 °C
 10900 psi

@Temperature 200 °F
 90°, Dry
80.7 MPa

@Temperature 25.0 °C
 11700 psi

@Temperature 77.0 °F
 90°, Dry
438 MPa

@Temperature 25.0 °C
 63500 psi

@Temperature 77.0 °F
 Open Hole Tensile, Dry
738 MPa

@Temperature 25.0 °C
 107000 psi

@Temperature 77.0 °F
 Quasi-Isotropic 25/50/25, Dry
1900 MPa

@Temperature -55.0 °C
 276000 psi

@Temperature -67.0 °F
 0°, Dry
2020 MPa

@Temperature 90.6 °C
 293000 psi

@Temperature 195 °F
 0°, Dry
2140 MPa

@Temperature 25.0 °C
 310000 psi

@Temperature 77.0 °F
 0°, Dry
Tensile Modulus 8.41 GPa

@Temperature 200 °C
 1220 ksi

@Temperature 392 °F
 90°, Dry
9.58 GPa

@Temperature 77.0 °C
 1390 ksi

@Temperature 171 °F
 90°, Dry
132 GPa

@Temperature 195 °C
 19100 ksi

@Temperature 383 °F
 0°, Dry
134 GPa

@Temperature -67.0 °C
 19400 ksi

@Temperature -88.6 °F
 0°, Dry
135 GPa

@Temperature 77.0 °C
 19600 ksi

@Temperature 171 °F
 0°, Dry
Flexural Yield Strength 1890 MPa

@Temperature 25.0 °C
 274000 psi

@Temperature 77.0 °F
 0°, Dry
Flexural Modulus 127 GPa

@Temperature 25.0 °C
 18400 ksi

@Temperature 77.0 °F
 0°, Dry
Compressive Yield Strength 186 MPa

@Temperature 25.0 °C
 27000 psi

@Temperature 77.0 °F
 After 2500 in-in-lb/in impact, Dry
193 MPa

@Temperature 25.0 °C
 28000 psi

@Temperature 77.0 °F
 After 2000 in-in-lb/in impact, Dry
221 MPa

@Temperature 25.0 °C
 32000 psi

@Temperature 77.0 °F
 After 1500 in-in-lb/in impact, Dry
239 MPa

@Temperature 25.0 °C
 34600 psi

@Temperature 77.0 °F
 Compression After Impact, Dry
345 MPa

@Temperature 25.0 °C
 50000 psi

@Temperature 77.0 °F
 After 500 in-in-lb/in impact, Dry
629 MPa

@Temperature 25.0 °C
 91200 psi

@Temperature 77.0 °F
 Compression Before Impact, Dry
1270 MPa

@Temperature 90.6 °C
 184000 psi

@Temperature 195 °F
 0°, Dry
1270 MPa

@Temperature 90.6 °C
 184000 psi

@Temperature 195 °F
 0°, Wet
1400 MPa

@Temperature 71.1 °C
 203000 psi

@Temperature 160 °F
 0°, Wet
1530 MPa

@Temperature 25.0 °C
 222000 psi

@Temperature 77.0 °F
 0°, Dry
1590 MPa

@Temperature -55.0 °C
 230000 psi

@Temperature -67.0 °F
 0°, Dry
Compressive Modulus 117 GPa

@Temperature 71.1 °C
 17000 ksi

@Temperature 160 °F
 0°, Wet
122 GPa

@Temperature 90.6 °C
 17700 ksi

@Temperature 195 °F
 0°, Dry
124 GPa

@Temperature -55.0 °C
 18000 ksi

@Temperature -67.0 °F
 0°, Dry
125 GPa

@Temperature 90.6 °C
 18100 ksi

@Temperature 195 °F
 0°, Wet
128 GPa

@Temperature 25.0 °C
 18600 ksi

@Temperature 77.0 °F
 0°, Dry
Shear Strength 77.9 MPa

@Temperature 90.6 °C
 11300 psi

@Temperature 195 °F
 0° Short Beam, Wet
84.1 MPa

@Temperature 71.1 °C
 12200 psi

@Temperature 160 °F
 0° Short Beam, Wet
101 MPa

@Temperature 90.6 °C
 14700 psi

@Temperature 195 °F
 0° Short Beam, Dry
105 MPa

@Temperature 93.3 °C
 15200 psi

@Temperature 200 °F
 +/- 45° In-Plane, Dry
114 MPa

@Temperature 25.0 °C
 16600 psi

@Temperature 77.0 °F
 +/- 45° In-Plane, Dry
117 MPa

@Temperature 25.0 °C
 16900 psi

@Temperature 77.0 °F
 0° Short Beam, Wet
128 MPa

@Temperature 25.0 °C
 18500 psi

@Temperature 77.0 °F
 0° Short Beam, Dry
164 MPa

@Temperature -55.0 °C
 23800 psi

@Temperature -67.0 °F
 0° Short Beam, Dry
Thermal Properties Metric English Comments
Maximum Service Temperature, Air 121 °C
250 °F
Epoxy Matrix Limit