Hexcel® F161 Epoxy Resin, 120 Kevlar Fabric

Category Polymer , Thermoset , Epoxy , Epoxy Cure Resin
Manufacturer Hexcel
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Hexcel® F161 Epoxy Resin, 120 Kevlar Fabric.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Hexcel designation: 120-38"-F161; Fiber: Kev. 49 195Information provided by HexCel
Mechanical Properties Metric English Comments
Tensile Strength, Yield 190 MPa

@Temperature 177 °C
 27600 psi

@Temperature 351 °F
 Wet
238 MPa

@Temperature 177 °C
 34500 psi

@Temperature 351 °F
 Dry
259 MPa

@Temperature 132 °C
 37600 psi

@Temperature 270 °F
 Wet
334 MPa

@Temperature 132 °C
 48400 psi

@Temperature 270 °F
 Dry
393 MPa

@Temperature -54.0 °C
 57000 psi

@Temperature -65.2 °F
 Dry
399 MPa

@Temperature 24.0 °C
 57900 psi

@Temperature 75.2 °F
 Wet
410 MPa

@Temperature 24.0 °C
 59500 psi

@Temperature 75.2 °F
 Dry
Tensile Modulus 17.9 GPa

@Temperature 177 °C
 2600 ksi

@Temperature 351 °F
 Wet
18.6 GPa

@Temperature 132 °C
 2700 ksi

@Temperature 270 °F
 Wet
19.0 GPa

@Temperature 177 °C
 2760 ksi

@Temperature 351 °F
 Dry
21.9 GPa

@Temperature 132 °C
 3180 ksi

@Temperature 270 °F
 Dry
24.9 GPa

@Temperature 24.0 °C
 3610 ksi

@Temperature 75.2 °F
 Wet
25.9 GPa

@Temperature 24.0 °C
 3760 ksi

@Temperature 75.2 °F
 Dry
27.3 GPa

@Temperature -54.0 °C
 3960 ksi

@Temperature -65.2 °F
 Dry
Compressive Yield Strength 52.0 MPa

@Temperature 177 °C
 7540 psi

@Temperature 351 °F
 Wet
70.0 MPa

@Temperature 132 °C
 10200 psi

@Temperature 270 °F
 Wet
90.0 MPa

@Temperature 177 °C
 13100 psi

@Temperature 351 °F
 Dry
117 MPa

@Temperature 132 °C
 17000 psi

@Temperature 270 °F
 Dry
139 MPa

@Temperature 24.0 °C
 20200 psi

@Temperature 75.2 °F
 Wet
199 MPa

@Temperature 24.0 °C
 28900 psi

@Temperature 75.2 °F
 Dry
222 MPa

@Temperature -54.0 °C
 32200 psi

@Temperature -65.2 °F
 Dry
Compressive Modulus 14.0 GPa

@Temperature 177 °C
 2030 ksi

@Temperature 351 °F
 Wet
15.7 GPa

@Temperature 132 °C
 2280 ksi

@Temperature 270 °F
 Wet
16.9 GPa

@Temperature 177 °C
 2450 ksi

@Temperature 351 °F
 Dry
18.4 GPa

@Temperature 132 °C
 2670 ksi

@Temperature 270 °F
 Dry
21.0 GPa

@Temperature 24.0 °C
 3050 ksi

@Temperature 75.2 °F
 Wet
24.1 GPa

@Temperature -54.0 °C
 3500 ksi

@Temperature -65.2 °F
 Dry
26.8 GPa

@Temperature 24.0 °C
 3890 ksi

@Temperature 75.2 °F
 Dry
Shear Strength 15.0 MPa

@Temperature 132 °C
 2180 psi

@Temperature 270 °F
 Short Beam
16.0 MPa

@Temperature 177 °C
 2320 psi

@Temperature 351 °F
 Short Beam
19.0 MPa

@Temperature 177 °C
 2760 psi

@Temperature 351 °F
 Short Beam
26.0 MPa

@Temperature 132 °C
 3770 psi

@Temperature 270 °F
 Short Beam
34.0 MPa

@Temperature -54.0 °C
 4930 psi

@Temperature -65.2 °F
 Short Beam
34.0 MPa

@Temperature 24.0 °C
 4930 psi

@Temperature 75.2 °F
 Short Beam
36.0 MPa

@Temperature 24.0 °C
 5220 psi

@Temperature 75.2 °F
 Short Beam
Descriptive Properties Value Comments
Cured Thickness per Ply (cm) 0.01
Laminate
Dry Resin Content (%) 52-58
Prepreg
Fiber Volume (%) 44
Laminate
Flow (%) 20-30