H.C. Starck Pure Molybdenum AB, Arc-Cast Bar

Category	Metal , Nonferrous Metal , Molybdenum Alloy , Pure Element
Manufacturer	H.C. Starck
Trade Name
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	H.C. Starck Pure Molybdenum AB, Arc-Cast Bar.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Arc-Cast BarDescription of Product: This specification covers carbon-deoxidized molybdenum wrought bar produced from ingots consolidated by the H.C. Stark consumable electrode vacuum-arc-casting process.Structure: Material can be supplied in the recrystallized condition.Information provided by H.C. Starck.

Mechanical Properties	Metric	English	Comments
Hardness, Vickers	<= 200 @Load 10.0 kg	<= 200 @Load 22.0 lb	mid-radius, recrystallized bar, all sizes; DPH (10 kg)
	205 - 240 @Load 10.0 kg, Diameter 73.03 - 88.9 mm	205 - 240 @Load 22.0 lb, Diameter 2.875 - 3.50 in	mid-radius; DPH (10 kg)
	210 - 250 @Load 10.0 kg, Diameter 47.63 - 73.03 mm	210 - 250 @Load 22.0 lb, Diameter 1.875 - 2.875 in	mid-radius; DPH (10 kg)
	215 - 260 @Load 10.0 kg, Diameter 28.57 - 47.63 mm	215 - 260 @Load 22.0 lb, Diameter 1.125 - 1.875 in	mid-radius; DPH (10 kg)
	225 - 270 @Load 10.0 kg, Diameter 22.2 - 28.57 mm	225 - 270 @Load 22.0 lb, Diameter 0.875 - 1.125 in	mid-radius; DPH (10 kg)
	230 - 280 @Load 10.0 kg, Diameter 3.17 - 22.2 mm	230 - 280 @Load 22.0 lb, Diameter 0.125 - 0.875 in	mid-radius; DPH (10 kg)
Tensile Strength	>= 448 MPa @Diameter 73.03 - 88.9 mm	>= 65000 psi @Diameter 2.875 - 3.50 in	ASTM E-8
	>= 483 MPa @Diameter 47.63 - 73.03 mm	>= 70000 psi @Diameter 1.875 - 2.875 in	ASTM E-8
	>= 517 MPa @Diameter 3.17 - 10.319 mm	>= 75000 psi @Diameter 0.125 - 0.40625 in	ASTM E-8
	>= 517 MPa @Diameter 28.57 - 47.63 mm	>= 75000 psi @Diameter 1.125 - 1.875 in	ASTM E-8
	>= 586 MPa @Diameter 22.2 - 28.57 mm	>= 85000 psi @Diameter 0.875 - 1.125 in	ASTM E-8
	>= 621 MPa @Diameter 10.319 - 22.2 mm	>= 90000 psi @Diameter 0.40625 - 0.875 in	ASTM E-8
Tensile Strength, Yield	>= 379 MPa @Diameter 3.17 - 10.319 mm, Strain 0.200 %	>= 55000 psi @Diameter 0.125 - 0.40625 in, Strain 0.200 %	ASTM E-8
	>= 379 MPa @Diameter 73.03 - 88.9 mm, Strain 0.200 %	>= 55000 psi @Diameter 2.875 - 3.50 in, Strain 0.200 %	ASTM E-8
	>= 414 MPa @Diameter 47.63 - 73.03 mm, Strain 0.200 %	>= 60000 psi @Diameter 1.875 - 2.875 in, Strain 0.200 %	ASTM E-8
	>= 448 MPa @Diameter 28.57 - 47.63 mm, Strain 0.200 %	>= 65000 psi @Diameter 1.125 - 1.875 in, Strain 0.200 %	ASTM E-8
	>= 483 MPa @Diameter 22.2 - 28.57 mm, Strain 0.200 %	>= 70000 psi @Diameter 0.875 - 1.125 in, Strain 0.200 %	ASTM E-8
	>= 517 MPa @Diameter 10.319 - 22.2 mm, Strain 0.200 %	>= 75000 psi @Diameter 0.40625 - 0.875 in, Strain 0.200 %	ASTM E-8
Elongation at Break	>= 10 % @Diameter 28.57 - 47.63 mm	>= 10 % @Diameter 1.125 - 1.875 in	ASTM E-8
	>= 10 % @Diameter 47.63 - 73.03 mm	>= 10 % @Diameter 1.875 - 2.875 in	ASTM E-8
	>= 10 % @Diameter 73.03 - 88.9 mm	>= 10 % @Diameter 2.875 - 3.50 in	ASTM E-8
	>= 15 % @Diameter 3.17 - 10.319 mm	>= 15 % @Diameter 0.125 - 0.40625 in	ASTM E-8
	>= 15 % @Diameter 10.319 - 22.2 mm	>= 15 % @Diameter 0.40625 - 0.875 in	ASTM E-8
	>= 15 % @Diameter 22.2 - 28.57 mm	>= 15 % @Diameter 0.875 - 1.125 in	ASTM E-8

Component Elements Properties	Metric	English	Comments
Carbon, C	<= 0.030 %	<= 0.030 %
Iron, Fe	<= 0.010 %	<= 0.010 %
Molybdenum, Mo	>= 99.95 %	>= 99.95 %	by difference
Nickel, Ni	<= 0.0020 %	<= 0.0020 %
Nitrogen, N	<= 0.0020 %	<= 0.0020 %
Oxygen, O	<= 0.0015 %	<= 0.0015 %
Silicon, Si	<= 0.010 %	<= 0.010 %