H.C. Starck 3203 Pure Molybdenum APL, Arc-Cast, Low Carbon Plate

Category Metal , Nonferrous Metal , Molybdenum Alloy , Refractory Metal , Pure Element
Manufacturer H.C. Starck
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF H.C. Starck 3203 Pure Molybdenum APL, Arc-Cast, Low Carbon Plate.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Arc-Cast Plate 3203 Low CarbonDescription of Product: This specification covers rolled plate of carbon-deoxidized molybdenum produced from ingots consolidated by the H.C. Starck consumable electrode vacuum-arc-casting process.Structure: Plate will be supplied in a stress-relieved condition unless otherwise requested.Information provided by H.C. Starck.
Mechanical Properties Metric English Comments
Tensile Strength >= 517 MPa

@Thickness 25.4 - 38.1 mm
>= 75000 psi

@Thickness 1.00 - 1.50 in
ASTM E-8
>= 586 MPa

@Thickness 12.7 - 25.4 mm
>= 85000 psi

@Thickness 0.500 - 1.00 in
ASTM E-8
>= 655 MPa

@Thickness 4.762 - 12.7 mm
>= 95000 psi

@Thickness 0.1875 - 0.500 in
ASTM E-8
Tensile Strength, Yield >= 414 MPa

@Strain 0.200 %,
Thickness 25.4 - 38.1 mm
>= 60000 psi

@Strain 0.200 %,
Thickness 1.00 - 1.50 in
ASTM E-8
>= 483 MPa

@Strain 0.200 %,
Thickness 12.7 - 25.4 mm
>= 70000 psi

@Strain 0.200 %,
Thickness 0.500 - 1.00 in
ASTM E-8
>= 552 MPa

@Strain 0.200 %,
Thickness 4.762 - 12.7 mm
>= 80000 psi

@Strain 0.200 %,
Thickness 0.1875 - 0.500 in
ASTM E-8
Elongation at Break >= 1.0 %

@Thickness 25.4 - 38.1 mm
>= 1.0 %

@Thickness 1.00 - 1.50 in
Transverse elongation varies according to the amount of reduction and cross-rolling necessary to roll to the desired size in this thickness range. Typical elongation will exceed 5% in most cases.; ASTM E-8
>= 2.0 %

@Thickness 12.7 - 25.4 mm
>= 2.0 %

@Thickness 0.500 - 1.00 in
Transverse elongation varies according to the amount of reduction and cross-rolling necessary to roll to the desired size in this thickness range. Typical elongation will exceed 5% in most cases.; ASTM E-8
>= 10 %

@Thickness 4.762 - 12.7 mm
>= 10 %

@Thickness 0.1875 - 0.500 in
ASTM E-8
Component Elements Properties Metric English Comments
Carbon, C <= 0.010 %
<= 0.010 %
Iron, Fe <= 0.010 %
<= 0.010 %
Molybdenum, Mo >= 99.97 %
>= 99.97 %
by difference
Nickel, Ni <= 0.0020 %
<= 0.0020 %
Nitrogen, N <= 0.0020 %
<= 0.0020 %
Oxygen, O <= 0.0015 %
<= 0.0015 %
Silicon, Si <= 0.010 %
<= 0.010 %