Grupo Repol Dinalon® A1S25 G25 PA66 25% Glass Fiber
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 30% Glass Fiber Filled |
| Manufacturer | Grupo Repol |
| Trade Name | Dinalon® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Grupo Repol Dinalon® A1S25 G25 PA66 25% Glass Fiber.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Mechanical properties for Dry As Molded samplesInformation provided by Grupo Repol
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.33 g/cc | 0.0480 lb/in³ | ISO 1183/A |
| Moisture Absorption at Equilibrium | <= 0.25 % | <= 0.25 % | Karl-Fischer; ISO 15512/A |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 175 MPa | 25400 psi | ISO 527 |
| Elongation at Break | 3.0 % | 3.0 % | ISO 527 |
| Tensile Modulus | 9.40 GPa | 1360 ksi | ISO 527 |
| Flexural Strength | 220 MPa | 31900 psi | ISO 178 |
| Flexural Modulus | 5.80 GPa | 841 ksi | ISO 178 |
| Charpy Impact Unnotched | 4.50 J/cm² @Temperature 23.0 °C |
21.4 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eU |
| Charpy Impact, Notched | 0.900 J/cm² @Temperature 23.0 °C |
4.28 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 250 °C | 482 °F | ISO 75/A |
| Vicat Softening Point | >= 230 °C | >= 446 °F | 50N; ISO 306 |