Gromax CCP PBT 3030-200HR 30% Glass Fiber Filled
| Category | Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) , Polybutylene Terephthalate (PBT), 30% Glass Fiber Filled |
| Manufacturer | Gromax |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Gromax CCP PBT 3030-200HR 30% Glass Fiber Filled.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Product Description: A glass fiber 30% reinforced injection molding grade. Characteristics:Excellent electrical property Excellent temperature resistance, high heat distortion temperature Excellent mechanic and chemical property Excellent weatherability Excellent wear property Excellent moldability High resistance to fuels, oil, fats and many solventsHigh hydrolysis resistanceInformation provided by Gromax Enterprises Corp.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.50 g/cc | 1.50 g/cc | ASTM D792 |
| Moisture Absorption | 0.0400 % @Time 86400 sec |
0.0400 % @Time 24.0 hour |
ASTM D570 |
| Linear Mold Shrinkage | 0.0020 - 0.0050 cm/cm @Thickness 1.60 mm |
0.0020 - 0.0050 in/in @Thickness 0.0630 in |
horizontal; ASTM D955 |
| 0.0080 - 0.014 cm/cm @Thickness 1.60 mm |
0.0080 - 0.014 in/in @Thickness 0.0630 in |
vertical; ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 121 | 121 | ASTM D785 |
| Tensile Strength | 127 MPa | 18300 psi | ASTM D638 |
| Elongation at Break | 4.0 % | 4.0 % | ASTM D638 |
| Flexural Strength | 202 MPa | 29300 psi | ASTM D790 |
| Flexural Modulus | 8.04 GPa | 1170 ksi | ASTM D790 |
| Izod Impact, Notched | >= 1.16 J/cm @Thickness 6.35 mm |
>= 2.17 ft-lb/in @Thickness 0.250 in |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 30.0 µm/m-°C | 16.7 µin/in-°F | ASTM D696 |
| Melting Point | 225 °C | 437 °F | DSC |
| Deflection Temperature at 0.46 MPa (66 psi) | 220 °C | 428 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 205 °C | 401 °F | ASTM D648 |
| Flammability, UL94 | HB @Thickness 0.800 mm |
HB @Thickness 0.0315 in |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | ASTM D257 |
| Surface Resistance | 1.00e+13 ohm | 1.00e+13 ohm | ASTM D257 |
| Dielectric Constant | 3.7 @Frequency 60.0 Hz |
3.7 @Frequency 60.0 Hz |
ASTM D150 |
| Dielectric Strength | 24.0 kV/mm @Thickness 2.00 mm |
610 kV/in @Thickness 0.0787 in |
ASTM D149 |
| Dissipation Factor | 0.0010 @Frequency 60.0 Hz |
0.0010 @Frequency 60.0 Hz |
ASTM D150 |
| Arc Resistance | 100 sec | 100 sec | ASTM D495 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 240 - 270 °C | 464 - 518 °F | |
| Nozzle Temperature | 260 - 270 °C | 500 - 518 °F | |
| Mold Temperature | 40.0 - 120 °C | 104 - 248 °F | suitable temperature 60-80°C |
| Injection Pressure | 50.0 - 120 MPa | 7250 - 17400 psi | |
| Hold Pressure | 30.0 - 80.0 MPa | 4350 - 11600 psi | |
| Back Pressure | 0.000 - 0.300 MPa | 0.000 - 43.5 psi | |
| Screw Speed | 60 - 120 rpm | 60 - 120 rpm | to be chosen in such a way that plasticizing time is just within cooling time |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Injection Rate | middle-fast |