Gromax CCP PBT 1100-220S

Category Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) , Polybutylene Terephthalate (PBT), Unreinforced, Molded
Manufacturer Gromax
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Gromax CCP PBT 1100-220S.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Product Description: PBT unreinforced and impact-modified injection molding grade. Characteristics:Low warp age, high toughness and excellent dimensional stabilityExcellent glossy surface and less-gas decompositionExcellent electrical property Excellent mechanic and chemical property Excellent weatherabilityExcellent wear property Excellent moldability High resistance to fuels, oil, fats and many solvents.Information provided by Gromax Enterprises Corp.
Physical Properties Metric English Comments
Specific Gravity 1.22 g/cc
1.22 g/cc
ASTM D792
Moisture Absorption 0.0600 %

@Time 86400 sec
0.0600 %

@Time 24.0 hour
ASTM D570
Linear Mold Shrinkage 0.0090 - 0.018 cm/cm

@Thickness 1.60 mm
0.0090 - 0.018 in/in

@Thickness 0.0630 in
horizontal; ASTM D955
0.012 - 0.021 cm/cm

@Thickness 1.60 mm
0.012 - 0.021 in/in

@Thickness 0.0630 in
vertical; ASTM D955
Mechanical Properties Metric English Comments
Hardness, Rockwell R 117
117
ASTM D785
Tensile Strength 39.2 MPa
5690 psi
ASTM D638
Elongation at Break 30 %
30 %
ASTM D638
Flexural Strength 55.0 MPa
7980 psi
ASTM D790
Flexural Modulus 1.57 GPa
228 ksi
ASTM D790
Izod Impact, Notched >= 4.41 J/cm

@Thickness 6.35 mm
>= 8.27 ft-lb/in

@Thickness 0.250 in
ASTM D256
Thermal Properties Metric English Comments
CTE, linear 90.0 µm/m-°C
50.0 µin/in-°F
ASTM D696
Melting Point 225 °C
437 °F
DSC
Deflection Temperature at 0.46 MPa (66 psi) 140 °C
284 °F
ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 55.0 °C
131 °F
ASTM D648
Flammability, UL94 HB

@Thickness 1.60 mm
HB

@Thickness 0.0630 in
Electrical Properties Metric English Comments
Volume Resistivity 1.00e+15 ohm-cm
1.00e+15 ohm-cm
ASTM D257
Surface Resistance 1.00e+13 ohm
1.00e+13 ohm
ASTM D257
Dielectric Constant 3.3

@Frequency 60.0 Hz
3.3

@Frequency 60.0 Hz
ASTM D150
Dielectric Strength 20.0 kV/mm

@Thickness 2.00 mm
508 kV/in

@Thickness 0.0787 in
ASTM D149
Dissipation Factor 0.0010

@Frequency 60.0 Hz
0.0010

@Frequency 60.0 Hz
ASTM D150
Arc Resistance 90 sec
90 sec
ASTM D495
Processing Properties Metric English Comments
Processing Temperature 230 - 260 °C
446 - 500 °F
Nozzle Temperature 245 - 250 °C
473 - 482 °F
Mold Temperature 30.0 - 100 °C
86.0 - 212 °F
suitable temperature 40-60°C
Injection Pressure 50.0 - 100 MPa
7250 - 14500 psi
Hold Pressure 30.0 - 70.0 MPa
4350 - 10200 psi
Back Pressure 0.000 - 0.300 MPa
0.000 - 43.5 psi
Screw Speed 60 - 120 rpm
60 - 120 rpm
to be chosen in such a way that plasticizing time is just within cooling time
Descriptive Properties Value Comments
Injection Rate middle-fast