Gromax BFG50-BN00N1 Nylon 6 60% Glass Filled (Dry)
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 60% Glass Fiber Filled |
| Manufacturer | Gromax |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Gromax BFG50-BN00N1 Nylon 6 60% Glass Filled (Dry).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Gromax Enterprises Corp.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.62 g/cc | 1.62 g/cc | ISO 1183 |
| Moisture Absorption | 0.760 % | 0.760 % | ISO 62 |
| Maximum Moisture Content | 0.10 | 0.10 | Karl Fischer |
| Linear Mold Shrinkage, Flow | 0.0010 cm/cm @Temperature 80.0 °C |
0.0010 in/in @Temperature 176 °F |
60x60x2 mm; ISO 294-4 |
| Linear Mold Shrinkage, Transverse | 0.0040 cm/cm @Temperature 80.0 °C |
0.0040 in/in @Temperature 176 °F |
60x60x2 mm; ISO 294-4 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 98 | 98 | [N/mm<sup>2<sup>]; ISO 7619 |
| Tensile Strength | 212 MPa | 30700 psi | 50 mm/min; ISO 527-1,-2 |
| Elongation at Break | 3.0 % | 3.0 % | 50 mm/min; ISO 527 |
| Tensile Modulus | 14.6 GPa | 2120 ksi | 1 mm/min; ISO 527-1,-2 |
| Flexural Strength | 366 MPa | 53100 psi | 5 mm/min; ISO 178 |
| Flexural Modulus | 12.8 GPa | 1860 ksi | 5 mm/min; ISO 178 |
| Izod Impact, Notched (ISO) | 19.0 kJ/m² | 9.04 ft-lb/in² | ISO 180-1A |
| Charpy Impact Unnotched | 10.0 J/cm² @Temperature 23.0 °C |
47.6 ft-lb/in² @Temperature 73.4 °F |
ISO 179-1eU |
| Charpy Impact, Notched | 1.91 J/cm² @Temperature 23.0 °C |
9.09 ft-lb/in² @Temperature 73.4 °F |
ISO 179-1A |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 220 °C | 428 °F | 10°C/min; ISO 11357-1,-3 |
| Deflection Temperature at 0.46 MPa (66 psi) | 226 °C | 439 °F | ISO 75-1,-2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 216 °C | 421 °F | ISO 75-1,-2 |
| Flammability, UL94 | HB @Thickness 1.60 mm |
HB @Thickness 0.0630 in |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 280 - 300 °C | 536 - 572 °F | ISO 294 |
| Mold Temperature | 80.0 - 120 °C | 176 - 248 °F | ISO 294 |
| Drying Temperature | 80.0 °C | 176 °F | |
| Dry Time | 2.00 - 6.00 hour | 2.00 - 6.00 hour |
Users viewing this material also viewed the following:
- LNP Stat-Kon® PDX-E-99689 CCS Polyetherimide, Carbon Fiber Reinforcement (discontinued **)
- Lehmann & Voss LUVOCOM® 3-7088/GY7012 Polyamide 6, with carbon fiber and glass fiber, low-warpage
- Malvern Minerals Wollastokup® FT Silane Treated Wollastonite
- ICE Steatite L-4
- Sapco Aluminum Nitride
- Teknor Apex Telcar® TL-1536D Thermoplastic Elastomer
- Voloknohim Nylon 6 Chips A Grade
- Ensinger TECANYL™ MT CF30 Autoclavable Polymer
- Chang Chun Plastic Longlite PM T357 Electrical Phenolic Molding Compound
- PolyOne Synprene® IT38-110 Thermoplastic Elastomer - SBC (discontinued **)
Copyright © lookpolymers.com All Rights Reserved