GrafTech eGRAF® HITHERM™ HT-1205 Graphite

Category Carbon , Graphite
Manufacturer GrafTech International
Trade Name eGRAF® HITHERM™
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF GrafTech eGRAF® HITHERM™ HT-1205 Graphite.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Made from natural graphite, eGRAF® HITHERM™ thermal interface materials are designed for use in applications requiring low contact resistance and high thermal conductivity. HITHERM™ material is offered in a variety of through thickness thermal conductivities, available in roll or die-cut form and can be laminated with plastics and adhesives. An economical thermal interface material, HITHERM™ products will not dry out and no outgassing occurs under vacuum conditions. The conformability of HITHERM™ materials optimizes thermal properties, ensures excellent contact, and is maintained for the life of the assembly. Typical applications include thermal interfaces, chip burn-in, chip testing fixtures, DC-to-DC converters, CPU modules, microprocessors, and hot and cold plates.
Physical Properties Metric English Comments
Thickness 127 microns
5.00 mil
Mechanical Properties Metric English Comments
Tensile Strength at Break 1.80 MPa
261 psi
ASTM-F152
Thermal Properties Metric English Comments
CTE, linear -0.400 µm/m-°C
-0.222 µin/in-°F
In-Plane
27.0 µm/m-°C
15.0 µin/in-°F
Through Thickness
Specific Heat Capacity 0.711 J/g-°C
0.170 BTU/lb-°F
Thermal Conductivity 10.0 W/m-K
69.4 BTU-in/hr-ft²-°F
Through Thickness; ASTM-D5470 Modified (at 110kPa/16 psi/1.1 bar)
150 W/m-K
1040 BTU-in/hr-ft²-°F
In-Plane; Angstrom's Method
Maximum Service Temperature, Air 400 °C
752 °F
Minimum Service Temperature, Air -40.0 °C
-40.0 °F
Flammability, UL94 V-0
V-0
Electrical Properties Metric English Comments
Electrical Resistivity 0.00100 ohm-cm
0.00100 ohm-cm
In-Plane
1.50 ohm-cm
1.50 ohm-cm
Through Thickness
Descriptive Properties Value Comments
Thermal Contact Impedance - Per Side (°C·cm²/W) 0.1
at 700 kPa/100 psi/6.9 bar
0.32
at 100 kPa/14.5 psi/1 bar